초록
Bond strength between alloy and ceramic plays an important role in deciding the quaring the processing of metalceramic restorations. Now the author had an experiment on the measurement of bond strength differences accoding to the contents of recast alloy used during the processing of metal-ceramic restorations. In the experiment, Anusavice's Planar Interface Shear Bond Test was employed to determine the bond strength. Total 25 specimens were divided as 5 groups, that is, 5 specimens in a group respections : Group I (new alloy 100%) Group II (new 75%$\cdot$recast 25%), Group III (new 50%$\cdot$recast 50%), Group IV (new 25%$\cdot$recast 75%), Group V(recast 100%). All specimens examined micropically and respective strength values of the group specimens were checked simultaneously. The results were as follows, 1. In the analtsis of variance the result showed the significant differences of 1%(P<0.01) among the each group classifid according to the recast contents. 2. When the interfaces of specimens were examined with an electron microscope, the air bubble were evenly occurred in all the specimens, and the occurrence frequencies and the sizes of air bubble were different between Group I and Group III, especially marked different Group I and Croup V. 3. In respective verification of each group through T-test, between Group I and Group II, between Group I and Group III did not show significant differences. 4. There was significant difference between Group I and Group IV, between Group I and Group V as 1%(P<0.01). 5. In the Shear Bond Test of all the groups, Croup V showed the lowest value. Explanatoion of Figures Fig 1. Main fracture type of metal-porcelain interlace showed in group I, II, III from shear Bond Test resets. Fig 2. Main fracture type of metal-porcelain interface showed In group Ⅳ, Ⅴ form shear Bond Test resets. Air bubble and their size appeared around interface of metal-porcelain. Fig 3. Group I, Fig 4. Group II Fig 5. Group III, Fig 6. Group IV, Fig 7. Group V.