A Study on the Synthesis and Physical Properties of Polyurethane Adhesives Modified with Butadiene Rubber

Butadiene 고무 변성 Polyurethane 접착제의 합성과 물성에 관한 연구

  • Hong, Suk-Pyo (Dept. of Chemical Tech., College of Eng., Chonbuk National University) ;
  • Choi, Sang-Goo (Dept. of Chemical Tech., College of Eng., Chonbuk National University)
  • 홍석표 (전북대학교 공과대학 공업화학과) ;
  • 최상구 (전북대학교 공과대학 공업화학과)
  • Published : 1990.09.30
Download PDF
⟨ Previous Next ⟩

Abstract

Rubber-modified polyurethane resin which was prepolymer type terminated with NCO, was synthesized by reacting isocyanate groups[NCO] and hydroxyl groups[OH]. Polybutadiene rubbers which had OH groups in the side of rubber chains, were charged at ratio $0%{\sim}40%$ of solid component in reactants. For products, physical properties were investigated experimentally. The results abtained in experiment were as follows. 1. Liquid resin and dried film was good solubility and clearity at less than 25%, 20% of rubber without being related to sort. 2. G-1000 showed better properties than R-45HT in solubility, dring time and adhesive strength. 3. Dring time and adhesive strength were considerably influenced by molecular weigh and structure of rubber. 4. In using 25% of mixed rubber(G-1000/R-45HT=50/50), It represented best properties in dring time(10 minute) and adhesive strength($23Kg/cm^2$).