A Study on Physical Properties of Epoxy Resin Filled with Surface-treated Silica: I. Surface-treating of Silica and Properties of Mixtures

표면처리된 실리카를 충전한 에폭시 수지계의 물성에 관한 연구 I. 실리카의 표면처리 및 혼합 물성

  • Hong, Suk-Pyo (Department of Chemical Technology, Chonbuk National University) ;
  • Choi, Sang-Goo (Department of Chemical Technology, Chonbuk National University)
  • 홍석표 (전북대학교 공과대학 공업화학과) ;
  • 최상구 (전북대학교 공과대학 공업화학과)
  • Received : 1990.08.27
  • Published : 1990.10.31
Download PDF
⟨ Previous Next ⟩

Abstract

Surface of crystalline silica was sequentially reacted with silane(A 187), liquid rubber(CTBNx8) and vinyl monomer(AA, MMA, 2-HEA, GMA) in existance of amines(TEA, CTMAB, BETAC) or peroxide(BPO). By mixing it with epoxy resin at a ratio 0~36%(volume %) of total component, liquid properties of mixtures was investigated experimentally. i) Coating ratio depended on quantity and sorts of catalyst. ii) Total coating of 2.5~5.8% was attained by using 0.1~2.0% of catalyst. iii) Treated surfaces represented each different features in according to sorts of treatment. iv) Silane/rubber or silane/rubber/vinyl represented lower viscosity and settling than non-treated or silane-treated.

결정성 실리카의 표면을 아민(TEA, CTMAB, BETAC) 및 과산화물(BPO) 촉매를 사용하여 실란(A 187), 액상고무(CTBNx8), 비닐단량체(AA, MMA, 2-HEA, GMA) 등으로 차례로 반응시켜 새로운 표면처리 실리카를 제조하였다. 표면처리 효과를 검토하기 위하여 실리카를 에폭시 수지에 전체 혼합물 중 0~36%(부피 %)의 범위로 혼합하여 혼합 점도 및 침전율의 변화를 시험하였다. 실험 결과 표면 피복량은 반응 촉매의 양과 종류에 의존하였으며, 촉매량 0.1~20%에서 실리카에 대한 피복량은 2.5~5.8% 범위의 값을 표시하였고, 실리카의 표면이 실란/고무, 실란/고무/비닐로 점차 처리됨에 따라서 무처리물이나 실란처리물에 비하여 점도가 저하되었으며, 침전율도 낮은 값을 표시하였다. 표면처리 상태는 처리제의 종류에 따라서 각기 다른 특성을 나타내었다.