Synthesis of $\alpha$-Sialon Ceramics from an Alkoxide and Their Mechanical Properties(I)

알콕사이드로부터 $\alpha$-Sialon 세라믹스의 제조 및 기계적 성질(I)

  • 이홍림 (연세대학교 공과대학 요업공학과) ;
  • 윤창현 (연세대학교 공과대학 요업공학과) ;
  • 조덕호 (국립공업시험원)
  • Published : 1991.02.01
Download PDF
⟨ Previous Next ⟩

Abstract

The powders of the system Si3N4-Y2O3-AlN were prepared using Si(OC2H5)4 and YCl3.6H2O together with commercial AlN powder. $\alpha$-Si3N4 was prepared by the carbothermal reduction and nitridation of the hydrolyzed gel at 135$0^{\circ}C$ for 10h in N2 atmosphere. YCl3.6H2O was observed to be changed to Y2O3 during the reaction. $\alpha$-Sialon(X=0.2, 0.4, 0.6) ceramics were obtained by hot-pressing the Si3N4-Y2O3-AlN mixture at 178$0^{\circ}C$ for 1h under 30 MPa. The content of $\alpha$-Sialon increased with increasing metal solubility(x value) and $\alpha$-Sialon single phase was obtained at the metal solubility of 0.6. With increasing metal solubility, flexural strength, fracture toughness and thermal shock resistence were decreased, while the microhardness was increased. Large elongated $\beta$-Si3N4 grains were mainly observed at lower metal solubility. Mechanical prorerties of the sintered ceramics with X=0.2 were measured as follows : flexural strength ; 650 MPa, fracture toughness ; 3.63 MN/m3/2, hardness ; 14.7 GPa, thermal shock resistence temperature ; 58$0^{\circ}C$.

Keywords

References

  1. 엔지니어링 세라믹스 이홍림(역)
  2. Progress in Nitrogen Ceramics v.3 Nitrogen Ceramics R.N. Katz;F.L. Riley(ed.)
  3. Special Ceramics of British Ceramic Proceedings No. 37 v.35 no.37 Reaction Mechanism in the Formation of Calcium and Yttria α-β Sialon Composites P.A. Walls;D.P. Thompson
  4. Special Ceramics of British Ceramic Proceedings No. 37 v.85 no.37 Sintering of Si₃N₄with Al₂O₃and Y₂O₃ M. Mitomo
  5. Ceramic Materials and Components for Engines Some Properties of α-Sialon Ceramics K. Ishizawa(et al.);W. Bunk(ed.);H. Hausner(ed.)
  6. Ceramic Materials and Components for Engines v.15 The Strength of α-Sialon Ceramics M. Mitomo;H. Tanaka;K. Muramatsu
  7. J. Am. Ceram. Soc. v.66 no.474 Formation of α-Sialon Solid Solutions in the System Si₃N₄-AIN-Y₂O₃ Z.K. Huang(et al.)
  8. J. Am. Ceram. Soc v.68 no.9 Effect of Nitrogen on the α/β Phase Conversion in Silicon Nitride M. Fukuhara
  9. J. Am. Ceram. Soc. v.69 no.10 Subsolidus Phase Relationships in Si₃N₄-AIN-Rare Oxide System Z.K. Huang(et al.)
  10. J. Mal. Sci . Lett. v.6 Two Dimensional Solid Solution Formation of Y-Containing α-Si₃N₄ S. Slasor;D.P. Thompson
  11. 연세대학교 대학원 석사학위 논문 알콕사이드로 부터 Si₃N₄와 Sialon의 합성 유영창
  12. Am. Ceram. Soc. Bull. v.56 no.9 Determination of Phase Content of Si₃N₄by X-ray Diffraction Analysis C. Gazzara;Messier
  13. Elements of X-ray Diffraction B.D. Cullity
  14. Progress in Nitrogen Ceramics K.H. Jack;F.L. Riley(ed.)
  15. J. Am. Ceram. Soc. v.59 Fracture Toughness Determination by Indentation A.G. Evans;E.A. Chales
  16. Progress in Nitrogen Cermics K.H. Jack;F.L. Riley(ed.)
  17. Modern Ceramic Engineering D.W. Richerson
  18. Yogyo-Kyokai-Shi v.94 Properties of α-Sialon Ceramics K. Ishzawa(et al.)
  19. Yogyo-Kyokai-Shi v.90 Strength of Hot-Pressed α-Sialon H. Danaka(et al.)
  20. Am. Ceram. Soc. Bull v.62 no.12 Fabrication and Properties of Dense Polyphase Silicon Nitride F.F. Lange
  21. 無機材硏硏究報告 no.32 三友
  22. Am. Ceram. Soc. Bull v.62 Thermal Expansion of 4-Sialon Ceramics M. Mitomo(et al.)
  23. 연세대학교 대학원 박사학위 논문 침전빕에 의한 Al₂O₃-ZrO₂계 미분체 제조 및 그 소결체의 특성 홍기곤