$Al_2O_3$-33Vol.% $SiC_w$의 고온피로에 미치는 피로하중주파수의 영향

Fatigue Frequency Effect of High Temperature Fatigue Fracture Behavior of $Al_2O_3$-33Vol.% $SiC_w$

  • 김송희 (강원대학교 재료공학과)
  • 발행 : 1991.10.01

초록

An investigation of the crack propagation behavior of Al2O3-33Vol.% SiCw at 140$0^{\circ}C$ was conducted with various loading frequencies. Higher crack propagation was observed in lower frequency and higher load ratios. Interface sliding fracture due to glassy phase from the oxidation of SiCw and cavitation along grain boundary of diffusional creep appeared to be the main mechanism of fatigue fracture in slower crack propagation while interface sliding and whisker pull out aided by glassy phase formation played main role of fatigue fracture for higher crack growth condition. The frequency effect on deformation behavior was discussed with a Maxwell model.

키워드

참고문헌

  1. High Tech Ceramics P. Vincenzini
  2. Advances in Fracture Research v.6 M.O. Speidel;D. Francois(ed.)
  3. American Society for Testing and Materials Fatigue at Elevated Temperature A.E. Carden;A.E. Carden(ed.);A.J. Mcevily(ed.);C.H. Walls(ed.)
  4. J. Am. Ceram. Soc. v.57 no.2 Relation between Strength, Fracture Energy and Microstructure of Hot-Pressed Si₃N₄ F.F. Lange
  5. J. Mater. Sci. v.13 The Structure of Slow Crack Interfaces in Silicon Nitride N.I. Tighe
  6. Metal Sci. Fracture Behavior of Ceramic Materials at High Temperature K. Kromp;R.F. Pabst
  7. J. Mater. Sci. v.22 Crack Resistance Curve of Alumina at High Temperature H. Wieninger;K. Kromp;R.F. Pabst
  8. Metall. Trans. v.5 no.5 Crack Propagation in ceramic Materials under Cyclic Loading Conditions A.G. Evans;E.R. Fuller
  9. J. Mater. Sci. v.22 no.4 Crack propagation in Ceramic under Cyclic Loads L. Ewart;S. Suresh
  10. J. Am. Ceram. Soc. v.71 no.3 Fracture of Si₃N₄-SiC Whisker Composites under Cyclic Loads S. Suresh;L.X. Han;J.J. Petrovic
  11. J. Am. Ceram. Soc. v.72 no.7 High-Temperature Fatigue of an Alumina-Silicon Carbide Composite under Cyclic Load: Mechanism of Fatigue Crack Tip Damage L.X. Han;S. Suresh
  12. High Temperature Fracture Toughness of Al₂O₃-$SiC_w$ Composite L.X. Han;S. Suresh;R. Warren
  13. Ph.D. Thesis Elevated Temperature Crack Growth Resistence of Alumina-Silicon-Carbide Composite under Static and Cyclic Load L.X. Han
  14. Introduction to Ceramics W.D. Kingery;H.K. Bowen;D.R. Uhlman
  15. Trans. ASME. Jour. Bas. Engr. D v.85 A Critical Analysis of Crack Propagation Laws P.C. Paris;F. Erdogan
  16. Creep, Viscoelasticity and Creep Fracture in Solids J. Gittus
  17. Elasticity and Anelasticity of Metals C. Zener