Influence of Thallium Carbonate on the Hydration of Tricalcium Silicate

Tricalcium silicate의 수화반응에 따른 $T1_2CO_3$의 영향

The influences of various concentrations of thallium carbonate on the hydration of tricalcium silicate which is widely used to the inorganic materials have been studied using an isothermal microcalorime-ter. The experimental results indicate that the hydration of tricalcium silicate is accelerated in the presence of thallium carbonate, namely the concentration of thallium carbonate is increased, the rate of hydration is also increased. The x-ray diffraction analysis shows that the concentration of tricalcium silicate decreases rapidly in the presence of thallium carbonate. Differential thermal analysis of tricalcium silicate hydrated in the persence of thallium carbonate indicates the presence of calcium carbonate. The nonevaporable water content and the degree of hydration of tricalcium silicate show that the accelerating action of thallium carbonate is more pronounced only during the early period of hydration. Analytical results of the liquid phase in contact with the tricalcium silicate paste indicate that the concentrations of calcium and hydroxyl ions are changed considerably in the presence of thallium carbonate.

규산삼석회$(C_3S)$의 수화반응에 있어서 $T1_2CO_3$의 농도변화에 따른 영향에 대해서 Isothermal microcalorimeter 등을 이용하여 조사한 결과, $T1_2CO_3$의 존재로 인하여 $C_3S$의 수화반응은 촉진되고 $C_3S$의 농도가 급격히 감소된다. 또 $T1_2CO_3$의 농도증가로 인해서 수화반응속도도 증가하고 있다. $T1_2CO_3$ 첨가에서 수화된 $C_3S$의 분석결과로는 반응초기에 $CaCO_3$가 나타나고 있으며, $T1_2CO_3$의 촉진작용이 수화반응의 초기에 있어서만 더욱 분명하게 나타나고 있음을 $C_3S$의 비휘발성 수분함량과 수화도로서 알수 있고 $C_3S$ paste와 접촉하고 있는 액상의 조성은 $T1_2CO_3$의 존재로 인하여 $Ca^(++)$이온과 $OH^-$ 이온의 농도가 상당히 변화하고 있음을 알 수 있다.