THE EFFECTS OF HEAT TREATMENT OF ORTHODONTIC WIRES

교정용 강선재의 열처리 효과에 관한 실험적 연구

The purpose of this study was to evaluate the effect of heat treatment on physical properties of 0.016' and 0.016' x 0.022' stainless steel wires. Temperature of heat treatment had intervals of $50^{\circ}C$ from $400^{\circ}C$ to $700^{\circ}C$, and time of heat treatment were 3, 6 and 9 minutes. Tensile tests were measured by ultimate tensile strength and yield strength. Bending tests were assessed by maximum bending force, recovery force, and stiffness. Torsion test was evaluated by torsion cycle until wires were fractured. The results were as follows: 1. In round wires, the highest value of ultimate tensile strength and yield strength were recorded of heat treatment at $500^{\circ}C$. In rectangular wires, the highest value of ultimate tensile strength were after 9 minutes at $400^{\circ}C,\;450^{\circ}C$ and 3, 6 minutes of heat treatment at $50^{\circ}C$, yield strength were the highest value after 3, 6 minutes of heat treatment at $500^{\circ}C$. 2. In both round and rectangular wires, maximum bending force and recovery force were the highest values after 6 minutes of heat treatment at $500^{\circ}C$. In round wires, highest value of stiffness were formed after 9 minutes at heat treatment at $500^{\circ}C$. In rectangular wires, the highest value of stiffness were for 6 minutes in $500^{\circ}C$. 3. In rectangular wires, torsion cycle was minimum after 6 minutes of heat treatment at $500^{\circ}C$. 4. In all of tension, bending, and torsion tests, the heat treated wires were softened over at $700^{\circ}C$. 5. In all of tension, bending, and torsion tests, physical properties of the wires were more influenced by the temperatures than the duration of the heat treatment.