Abstract
$Na_2O-CaO-MgO-Al_2O_3-SiO_2$ glass was taken as a basic glass and then $Li_2O$ O.5wt%, $K_2O$ 2.0wt% were substituted to $Na_2O$content, MgO 12.0wt %, ZnO 6.0wt % to CaO content. And also nucleation agent $ZrO_2 and $CaF_2$ were added to 1-2wt% respectively. The crystal according to the compositions appeared wollastonite, diopside and diopside.tremolite. The glasses substituted NazO by LizO was decreased thermal expansion coeffcient but substituted by ZnO was opposite direction and both of them increased bending strength. In the ratio of ZrOz to CaF, each 1: 1 and 1: 2 have shown considerable crystal growth at $1000^{circ}C~1050^{\circ}C$ and high bending strength, but the glass in the ratio 1: 2 have shown lowest thermal expansion coefficient. The activation energy was at the glass in the ratio of ZrO, to CaFz 1:2 evaluated 55.24kvsl/mol by Ozawa type and 53.05kal/mol by kissinger type.
$Na_2O-CaO-MgO-Al_2O_3-SiO_2$계를 기본조성으로 하여 $Na_2O$에 $Li_2O 0.05wt%, $K_2O$를, CaO에 MgO 12.0wt%, ZnO 6.0%를 각각 치환하여 조성을 선정하였다. 기본 유리조성의 결정상은 wollastonite이고, 치환된 조성들은 diopside, diopside.tremolite의 혼정이 나타났다. $Na_2O$를 $Li_2O$로 치환한 시편은 열팽창계수가 감소하였지만 CaO를 ZnO로 치환한 시편은 열팽창 계수가 증가하였다. 곡강도에 있어서는 치환에 따라 모두 증가시켰다. 핵행성제로 $ZrO_2와 $CaF_2$를 각각 1~2wt%의 변화를 시켜본 결과 핵형성제 $ZnO_2$와 $CaF_2$가 1:1, 1:2인 시편은 $1000~1050^{\circ}C$온도에서 급격한 결정성장을 보였으며 1:2시편이 가장 낮은 열팽창 계수값을 나타냈다. 곡강도는 모두 $1000~1050^{\circ}C$의 결정화 온도 범위에서 높은 강도를 나타내었다. 결정화에 필요한 활성화 에너지는 Ozawa와 Kissinger식으로 plot하여 각각 55.24kcal/mol과 53.05kcal/mol이다.