A Synthesis of $(Ba_{1-x}Sr_x)TiO_3$ Powders by Sol-Gel Route

졸-겔법을 이용한$(Ba_{1-x}Sr_x)TiO_3$분말합성

  • Kim, Young-Seok (Dept. of Inorganic Mat. Eng., Seoul National Univ.) ;
  • Kim, Duk-Jun (Dept. of Inorganic Mat. Eng., Seoul National Univ.) ;
  • Kim, Hwan (Dept. of Inorganic Mat. Eng., Seoul National Univ.)
  • 김영석 (서울대학교 공과대학 무기재료공학과) ;
  • 김덕준 (서울대학교 공과대학 무기재료공학과) ;
  • 김환 (서울대학교 공과대학 무기재료공학과)
  • Published : 1992.04.01
Download PDF
⟨ Previous Next ⟩

Abstract

Using $Ba(OH)_2{\cdot}8H_2O, \;Sr(OH)_2{\cdot}8H_2O$ and $Ti(i-OC_3H_7)_4$, fine $(Ba_{1-x}, \;Sr_{x})TiO_3$ powders were synthesized through sol-gel process. The particle size of the powders calcined at $700^{\cric}C$ proved to be 20-40nm by the observation of TEM micrographs and measurement of BET specific surface area. The analysis of XRD patterns showed that the phase of the powders was cubic, and it was identified with the lattice parameters determined through XRD patterns and the shift of (112) peaks that the solid solution powders were synthesized. It was expected through the analysis of relative ratio of cations and the uniformity of compositions in the powders examined by EDAX analysis and relative dielectric constant measurements for sintered body that the distribution of cations was uniform in particle unit.

본 연구에서는 $Ba(OH)_2{\cdot}8H_2O,\;Sr(OH)_2{\cdot}8H_2O$ 및 $Ti(i-OC_3H_7)_4$를 사용하여 졸-겔법에 의해 미세한 $(Ba_{1-x}Sr_{x})TiO_3$ 분말을 제조하였다. TEM 관찰, BET 비표면적측정 및 XRD회절도의 분석결과 $700^{\cric}C$에서 하소한 뚠말의 입자크기는 20~40nm이고 입방정상으로 존재하였다. 또한 XRD 회절도고부터 계산된 격자상수 및 (112)피크의 이동으로부터 고용체분말이 형성되었음을 확인할 수 있었다. 제조된 분말에서의 EDAX 분석을 통한 양이온들의 상대적인 비율 및 소결체에 대한 유전상수의 측정결과로부터 제조된 분말에서 양이온들의 분포가 입자단위에서 균질함을 예상할 수 있었다.