Mechanical property of Diglycldyl ether of bisphenol A-Methylene dianiline System with Succinonitrile

Diglycidyl ether of bisphenol A-Methylene dianiline-Succinonitrile계의 역학적 성질

The new epoxy resin, diglycidyl ether of bisphenol A(DGEBA)/4, 4'-methylene dianiline (MDA)/succinonitrile system, containing the reactive additive succionitrile was investigated through the impact test and the stress-strain test on the basis of the behavior of cure reaction and the cure mechanism. The new epoxy resin system, having the different succinonitrile contents, were cured at $80^{\circ}C$for 1.5 hour and then in order to cure completely at $150^{\circ}C$ for 1 hour. It was shown that as the succinonitrile content increased, impact strength was gradually increased, tensile strength was decreased, almost constantly Young's modulus was sustained and elongation was increased until the succinonitrile content was increased to 10phr, and then decreased. From the experimental results, it can be concluded that the chemical bonding length between the main chains was extended by adding the reactive additive succinonitrile. It was also found that the flexibility of epoxy resin was improved by adding the succinonitrile.

Succinonitrile을 첨가한 새로운 에폭시 수지, diglycidyl ether of bisphenol A(DGEBA)/4, 4'-methylene dianiline(MDA)/succinonitrile(SN)계의 역학적 성질을 충격 저항실험과 응력 변형실험을 통하여 곁화반응 특성과 반응기구를 근거로 하여 고찰하였다. DGEBA/MDA계에 각각 다른 succinonitrile의 함량을 포함하는 계를 $80^{\circ}C$에서 1.5시간 동안 경화시킨 후 완전히 경화를 이루기 위하여 $150^{\circ}C$에서 1시간 동안 경화시킨 후 시험한 결과 Succinonitrile의 함량이 증가함에 따라 본 계의 충격강도는 점차적으로 증가하였으나 인장강도는 감소하였다. 그리고 Young률은 거의 일정하게 나타났으며, 신도는 succinonitrile의 함량이 10phr에서 최대값을 보였다. 본 실험으고부터 얻은 결과는 succinonitrile이 첨가됨으로써 주 사슬간의 결합길이가 연장되었기 때문임을 알았고, 적당량의 succinonitrile을 첨가함으로 에폭시 수지의 유연성이 개선됨을 알 수 있었다.