A study on the effect of Ni-rich phase on the stress-rupture properties of Ni microalloyed W

W 활성소결체의 Ni-rich 상의 양이 응력 파단 성질에 미치는 영향에 관한 연구

  • Park, Dae-Gyu (Semiconductor Research and Development Laboratory, Hyundai Electronics Industries Co.Ltd.,) ;
  • Kim, Su-Seong (Department of Metallurgical Engineering, Hnayang University) ;
  • Lee, Kyung-Sub (Department of Metallurgical Engineering, Hnayang University)
  • 박대규 (현대전자 반도체연구소 공정개발 2실) ;
  • 김수성 (한양대학교 금속공학과) ;
  • 이경섭 (한양대학교 금속공학과)
  • Published : 1992.08.01

Abstract

The effect of Ni-rich phase on the stress-rupture properties of Ni mlcroalloyed W were studied using direct load creep tester at 100$0^{\circ}C$, 110$0^{\circ}C$, and 120$0^{\circ}C$ in $H_2.$ The stress rupture strength of 100hrs. of W-0.4wt% Ni was 43% higher at 100$0^{\circ}C$ and 35% higher at 110 $0^{\circ}C$than that of W-0.2wt% Ni due to the larger initial grain size, the higher relative density and the higher grain growth during test. That of W-0.8wt% Ni was 90% higher at 100$0^{\circ}C$ and 60% higher at 110$0^{\circ}C$ than that of W-0.2wt% Ni. The activation energy of W-0.4wt% Ni for creep was 81.3 Kcal/mole. It was considered that creep deformation was controlled by the diffusion of W in the Ni rich phase between the grains and the deformation of grains. All of the specimens showed intergranular fracture by grain boundary cavitation and growth of cavity throughout the entire spcimen cross-section.

W-0.4wt% Ni, W-0.8wt% Ni 활성 소결체의 Ni rich상의 양이 응력 파단 성질에 미치는 영향을 조사하기 위하여, direct load creep tester를 사용, 100$0^{\circ}C$~120$0^{\circ}C$, 수소 분위기에서 응력 파단시험을 하였다. 100시간 응력 파단 강도는 니켈 함량이 0.4wt%, 0.8wt%로 증가 함에 따라, W-0.2wt% Ni의 경우와 비교하여 100$0^{\circ}C$에서 43%, 90%, $1100^{\circ}C에서$ 35%, 60% 높았으며, 이는 초기 결정립 조대화, 비이론밀도의 상승과 시험 중 결정립 성장 때문으로 생각된다. W-0.4wt% Ni의 크리프변형 활성화 에너지는 81.3kca1/mol으로, 변형기구는 Ni rich 상을 통한 W 확산과 결정립 내부 변형이다. 응력 파단 시험 후, 파단면은 입계 파괴 양상을 나타내었다. 소결시 생성된 고립 기공이 결정입계에 있는 Ni rich상을 따라 전파하였기 때문이다.