Permeability Aftereffect in FeCuNbSiB Alloy

FeCuNbSiB 합금의 투자율 여효

  • Lee, Yong-Ho (Department of Physics, Jeonbuk National University) ;
  • Sin, Yong-Dol (Department of Physics, Jeonbuk National University) ;
  • No, Tae-Hwan (Magnetic Alloys Lab, Korea Institute of Science and Technology) ;
  • Gang, Il-Gu (Magnetic Alloys Lab, Korea Institute of Science and Technology)
  • 이용호 (전북대학교 물리학과) ;
  • 신용돌 (전북대학교 물리학과) ;
  • 노태환 (한국과학기술연구원 자성합금연구실) ;
  • 강일구 (한국과학기술연구원 자성합금연구실)
  • Published : 1992.11.01
Download PDF
⟨ Previous Next ⟩

Abstract

Annealing effects on the permeability aftereffect(disaccommodation) of liquid quenched single strip $Fe_{73.5}Cu_1Nb_3Si_{16}B_{6.5}$ alloys were investigated with pulse method. The initial susceptibility X, $B_{10},$ (the flux density at 10 Oe) and disaccommodation intensity D (D = [X(1 s)-X(64 s)]/X(1 s), where X(1 s) and X(64 s) are the susceptibility of 1 and 64 s of rest time after A. C. demagnetization) were about 800, 0.8 T and 16 %, respectively. The soft magnetic properties were improved with isothermal annealing for 1 hour at $300{\sim}600^{\circ}C.$ X, $B_{10},$ and D at $570^{\circ}C$ of optimum annealing temperature were 15000, 1.2 T and 1.1 %, respectively. The origin of the change of characteristics were examined with fine crystalline structure and magnetostriction.

액체급냉법으로 제작한 단일박대형 $Fe_{73.5}Cu_1Nb_3Si_{16}B_{6.5}$ 합금의 투자율 여효에 대한 열처리 효과를 펄스측정법으로 조사하였다. 미열처리 시료의 자화율 X와 인가자기장이 10 Oe 때의 자속밀도 $B_{10}$은 약 800과 0.8 T 였으며, 교류소자후 1초에서 64초 사이의 X의 변화율 D는 약 16%였다. $300^{\circ}C$에서 $600^{\circ}C$ 사이의 1시간의 등온 열처리에 의하여 연자기특성은 향상하였으며 최적 열처리온도 $570^{\circ}C$에서 X, $B_{10},$ D는 각각 15000, 1.2 T, 1.1 % 이였다. 열처리에 의한 특성의 변화의 원인을 미세결정립의 크기와 자기변형등에 연관하여 고찰하였다.