Magnetic Properties of $NdFe_{10.7}TiB_{0.3}N_x$ and $NdFe_{10.7}TiMo_{0.3}N_x$

$NdFe_{10.7}TiB_{0.3}N_x$ 및 $NdFe_{10.7}TiMo_{0.3}N_x$의 자기특성

It has been found that B is very effective for the increase of magnetization and Curie temperature in $NdFe_{11}TiN_x$-type compounds having $ThMN_{12}$-type structure. Experimental results have shown that magnetization and Curie temperature of $NdFe_{10.7}TiB_{0.3}N_x$ are 148 $Am^2$/kg and $560^{\circ}C,$ respectively, by about 20 $Am^2$/kg and $90^{\circ}C$ higher than those of $NdFe_{10.7}Ti_{1.3}N_x.$ On the other hand, Mo is effective for the increase of anisotropy field, and it seems to strongly inhibit the formation of ${\alpha}-Fe$ phase during the nitrification treatement. The anisotropy field of $NdFe_{10.7}TiMo_{0.3}N_x$ is about 7960 kA/m (100 kOe) which is about 1590 kA/m (20 kOe) higher than that of $NdFe_{10.7}Ti_{1.3}N_x$.

$ThMN_{12}$ 구조를 갖는 $NdFe_{11}TiN_x$ 형 화합물에서 B 이 자화 및 큐리온도의 상승에 매우 효과적임이 밝혀졌다. $NdFe_{10.7}TiB_{0.3}N_x$ 의 자화 및 큐리온도는 $NdFe_{10.7}Ti_{1.3}N_x$ 의 경우에 비하여 각각 20 $Am^2$/kg (20 emu/g) 및 $90^{\circ}C$가 높은 148 $Am^2$/kg (148 emu/g) 및 $560^{\circ}C$를 나타내었다. 한편, Mo은 이방성자장의 증가에 효과적이며, 또한, 질화처리시 ${\alpha}-Fe$의 생성 억제에 효과적인 것으로 추측된다. $NdFe_{10.7}TiMo_{0.3}N_x$ 의 이방성자장은 약 7960 kA/m (100 kOe) 로 $NdFe_{10.7}Ti_{1.3}N_x$ 의 경우에 비하여 약 1590 kA/m (20 kOe) 가 증가한 결과를 보였다.