A Study on Optimization of Physical Properties of Acrylic Pressure Sensitive Adhesives

아크릴 점착제의 최적물성에 관한 연구

The effects of functional monomers on the pressure sensitive adhesive proporties were studied. Acrylic acid and other monomers were copolymerized by radical solution polymerization and their properties were measured. The desirability function methodology was applied to obtain optimum pressure sensitive adhesive properties. Acrylic acid showed more effective than acrylamide on peel strength increase. On the other hand acrylamide showed more effective than acrylic acid on tack decrease. The optimum monomer ratio of the acrylic pressure sensitive adhesive recipe containing n-butylacrylate 81.7 mole%, acrylic acid 8.0 mole%, acrylamide 2.1 mole% and vinylacetate 8.2 mole% was obtained to result from the statistical analysis with the desirability function methodology. The estimated regression equation of desirability function(D) is as follows: $D=.857+.072X_1-.114X_2-.027X_3-.126X_1{^2}-.046X_1{\cdot}X_2-.063X_1{\cdot}X_3-.152X_2{^2}+.027X2{\cdot}X_3-.120X_3{^2}$ $X_1$:coded acylic acid, $X_2$:coded acylamide, $X_3$:coded vinylacetate

기능성 단량체가 점착물성에 미치는 영향을 알아보기 위하여 아크릴산과 기타 단량체로 아크릴 수지를 라디칼 용액중합을 이용하여 4원공중합시킨 후 물성을 측정하였으며, 또한 최적 점착 물성을 얻기 위하여 통계적 분석 방법을 이용하여 검토하였다. 점착물성에 있어서 아크릴산이 아크릴아미드보다 점착력의 증가에 미치는 영향이 컸다. 반면에 tackiness의 감소에 있어서는 아크릴아미드의 영향이 아크릴산 보다 컸다. 통계적 방법을 인용하여 점착물성 중 점착력, tackiness 그리고 응집력을 최적화 시킨 결과 단량체의 성분 비율은 부틸 아크릴레이트 81.7 mole%, 아크릴산 8.0 mole%, 아크릴아미드 2.1 mole%, 비닐아세테이트 8.2 mole% 일 때로 나타났고 이 때의 추정 회귀식은 다음과 같았다. $D=.857+.072X_1-.114X_2-.027X_3-.126X_1{^2}-.046X_1{\cdot}X_2-.063X_1{\cdot}X_3-.152X_2{^2}+.027X2{\cdot}X_3-.120X_3{^2}$ $X_1$:coded acylic acid, $X_2$:coded acylamide, $X_3$:coded vinylacetate