Sintering and Isothermal Phase Transformation of Calcia Stabilized Tetragonal Zirconia Polycrystals

칼시아 안정화 정방정 지르코니아(Ca-TZP)의 소결 및 등온상전이 거동

  • 곽효섭 (전남대학교 무기재료공학과) ;
  • 백용혁 (전남대학교 무기재료공학과) ;
  • 이종국 (조선대학교 재료공학과)
  • Published : 1993.02.01
Download PDF
⟨ Previous Next ⟩

Abstract

Calcia stabilized zirconia polycrystal (Ca-TZP) powders synthesized by hydrothermal treatment was sintered at a temperature range of $1200^{\circ}C~1400^{\circ}C$ and investigated the properties of sintered body and the behaviors of isothermal phase transformation. The sintered bodies of Ca-TZP were shown the density of about 97% and the average mean tetragonal grain size of about $0.1~0.25{\mu}m$. Also, Ca-TZP specimen was more stable during aging at $250^{\circ}C$ than that of Y-TZP ceramics.

수열반응법으로 합성한 칼시아 안정화 지르코니아 분말을 $1200^{\circ}C~1400^{\circ}C$의 온도에서 소결시켜 Ca-TZP 세라믹스를 제조한 후 소결체의 물성과 $250^{\circ}C$에서의 등온 상전이 거동을 고찰하였다. 그 결과 소결밀도가 약 97%이고 평균 입자크기가 $0.1~0.25{\mu}m$인 미세한 구조의 정방정상 지르코니아 다결정체(Ca-TZP) 세라믹스를 제조할 수 있었다. 이러한 Ca-TZP 세라믹스는 종래의 Y-TZP 세라믹스에 비햐여 열안정성이 매우 우수하였다.