Abstract
A relationship $(T_c = -17.869C^2+1840.2C-46623)$ between Curie Temperature$(T_c)$ and (C), $Li_2O$ mole percent(%) was established from the measurement results of Curie temperature $(T_c)$) analysed by DTA(Differential Thermal Analysis) in the range from 48.50 to 49.00 $Li_2O$ mole %. Congruent melt composition of $LiTaO_3$ single crystal was to be 48.65 $Li_2O$ mole % and its Curie temperature was also determined to be $610{\pm}1^{\circ}C$ from the results of Curie temperature difference, ${\Delta}T (T_{c(Top)}-T{_c(Tail)})$ of Czochralski grown $LiTaO_3$ crystals and the distribution coefficient(k). The k was calculated from $LiO_2$ mole ratio of initial melt to final melt and initial crystal to final crystal in the range from 48.60 to 48.70 $Li_2O$ mole %.
열분석(DTA : Differential Thermal Analysis) 방법에 의한 퀴리온도$(T_c)$ 측정방법으로부터 48.50에서 49 $Li_2O$ mole %까지의 퀴리온도$(T_c)$와 $Li_2O$ mole %(C)의 관계식 $(T_c = -17.869C^2+1840.2C-46623)$을 구하였다.$LiTaO_3$ 단결정의 congruent 조성을 결정하기 위하여 48.60 부터 48.70 mole %까지의 영역에서 쵸크랄스키법으로 $LiTaO_3$ 단결정을 육성하고 Top과 Tail 결정에서의 퀴리온도 차이,${\Delta}{T_c} (T_{c(Top)}-T{_c(Tail)})$ 그리고 결정성장 초기와 말기의 융액과 결정의 조성비로부터 분배계수(k)를 구하였다. 이 결과로부터 결정된 congruent 조성은 48.65 mole %였으며 그때의 $(T_c)$ 값은 $610{\pm}1^{\circ}C$였다.