Abstract
The glasses, which the $\beta$-spodumene as the principal crystalline phase could be precipitated, were melted by adding >, $P_2O_5, TiO_2, ZrO_2 in the Li_2O-Al_2O_3-SiO_2$ system. In order to achieve the glass-ceramic body of near-theoritical density by sintering method, the optimum condition of heat treatment, the effect of glass powder size and the properties were investigated by DTA, XRD, bulk density, thermal expansion and SEM. Addition of $P_20_5$ imProved the tendency of sintering and the sample with 9wt% $P_20_5$ content was the most dense OOdy by sintering method. The optimum condition of heat treatmemt was sintered for densitification at $740^{\circ}C$ and crystallized at $950^{\circ}C$. In the optimum condition, the relative density was above 90% and the thermal expansion was negative about $-1{\times}10^{-7}/^{\circ}C$.
$Li_2O-Al_2O_3-SiO_2$계 유리조성에서, 특히 주결정상으로 $\beta$-spodumene을 석출시킬 수 있는 조성영역에서 $P_2O_5, TiO_2, ZrO_2$ 등을 첨가하여 용융한 후 소결법을 이용하여 이론밀도에 가까운 결정화 유리를 만들기 위한 최적 열처리 조건, 유리 분말의 입도 변화에 따란 영향과 그 때의 물성을 시차열분석, X-선 회절분석, 비중 측정, 열팽창 측정, 전자현미경 관찰 등을 통하여 연구하였다. $P_2O_5$를 첨가하여 소결법으로 결정화할 때 소결을 증진시키는 효과가 있었으며 9wt% 첨가한 경우가 가장 치밀한 것으로 나타났다. 최적의 열처리 조건은 $740^{\circ}C$에서 소결하여 치밀화를 시키고$ 950^{\circ}C$에서 결정화를 시켰을 때로서 상대밀도는 90% 이상이었으며 열팽창계수는 $-1{\times}10^{-7}/^{\circ}C$ 정도로서 부팽창인 것으로 나타났다.