Abstract
Abstract The sintering behavior of the mechanically alloyed AI-8wt%Fe power during vacuum hot pressing was investigated and high temperature deformation behavior of the sintered specimen was studied through compression tests at various strain rates in the temperature range between 35$0^{\circ}C$ and 45$0^{\circ}C$. In 'addition, thermal stablity of the sintered specimem was examined by hardness measurement after annealing the spcimem for 60 hours in the temperature range of 30$0^{\circ}C$ ~50$0^{\circ}C$. The compressive stress increased rapidly with strain and reached the maximum point at the strain about 3%. With slight decrement after reaching the maximum point, the flow stress became constant up to the strain of 30% and it was considered to be due to equilibrium between work hardening and dynamic recrystallization. The hardness of the 60 hrs annealed specimens began to decrease rapidly at 40$0^{\circ}C$ .
기계적 합금화 방법으로 제조된 A-8wt%Fe합금분말의 진공고온 소결거동을 분석하였고 이 소결체의 고온변형거동을 연구하기 위하여 35$0^{\circ}C$-45$0^{\circ}C$의 온도 범위에서 여러 변형률속도로 압축 시험을 수행하였다. 또한 이 소결체의 열적안정성을 조사하기 위하여 30$0^{\circ}C$-50$0^{\circ}C$온도 범위에서 각각 60시간 동안 열처리한 후 경도시험을 수행하였다. 압축응력은 변형률이 증가함에 따라 급격히 증가하여 변형률 약 3%에서 최대응력에 이르렀으며, 최대응력 이후 다소 연화현상을 보인 후 유동응력은 가공경화돠 동적 재결정의 평형률 30%까지 일정하였다. 또한 60시간 열처리에 따른 소결시편의 경도는 40$0^{\circ}C$에서 부터 급격히 감소하였다.