Abstract
Abstract Alloying elements such as AI, Ti, Nb and B in the extra low carbon AI-killed steel precipitate as nitrides or carbides and change the recrystallization texture structure of the steel during heattreatment with the result of strong effects on the deep drawability of the steel sheet. In this study the effects of fine precipitates such as nitrides and carbides on the texture of extra low carbon steels into which Ti, Nb, B, P, Si and Mn were added as alloying elements were investigated by means of TEM, SEM and optical microscopic analyses. Fine N$b_2$C and T$i_2$AIN precipitates are mainly observed in the steel containing both Nb and Ti, while fine AIN and coarse BN precipitates are observed in the Nb~containing steel and coarse T${i_4}{N_3}$ and ${N_10}{N_22}$/T$i_68$ precipitates are observed in the Ti-containing steel. The grain size of the Ti containing steel is larger than that of the Nb containing steel and that of the one containing both Nb and Ti.
극저탄소 알루미늄 킬드강내에 합금원소로 첨가된 Al, Ti, Nb, B등은 열처리 공정중 질화물이나 탄화물로 석출되어 강의 재결정집합조직을 변화시킴으로써 강판재의 디입드로잉 특성에 결정적인 영향을 미친다. 본 연구에서는 Ti및 Nb를 단독으로 또는 동시에 첨가한 데 이어, B, P, Si 및 Mn등을 추가로 첨가한 극저탄소 고강도 강판의 집삽조직에 미치는 질화물, 탄화물과 같은 미세 석출물의 영향을 TEM, SEM, 광학현미경분석에 의하여 조사하였다. Nb 및 Ti를 동시에 첨가한 강에서는 미세한 N$b_2$C 및 T$i_2$AIN가 주로 석출되는 반면, Nb를 단독으로 첨가한 강에서는 미세한 AIN 및 조대한 BN이 석출되고,Ti를 단독으로 첨가한 강에서는 비교적 조대한 T${i_4}{N_3}$및 조대한 ${N_10}{N_22}$/T$i_68$이 석출되는 것으로 관찰되었다. 또한 이러한 탄질화물들의 석출에 의하여 세 강이 서로 다른 결정입도를 나타내는데, 결정입도는 Nb 및 Ti동시첨가강과 Nb단독첨가강이 서로 비슷하고, Ti단독첨가강이 가장 큰 것으로 나타났다.