Abstract
Abstract In this work. gasification of graphite cores from nickel-coated graphite composite powders was carried out to munufacture the hollow nickel metal powders which can be used as a raw materials for porous nickel metal strips. Graphite cores were gasified by $H_2O-H_2$ mixture gases at the temperature between $800^{\circ}C$ and $900^{\circ}C$ and nearly all removed from the composite powders within 1 hour. The hollow nickel metal powders prepared from 82.2wt. % Ni-17.8wt. % C composite powders which have the graphite cores of 21${\mu}$m average size were pressed and sintered at $1150^{\circ}C$ for 1 hour in vacuum furnace. The porosities of green and sintered compacts were 45% and 30%. respectively, and pores were distributed very homogeneously in the sintered compact. It was confirmed that pore distribution and porosity in porous materials can be easily controlled by using hollow powders as a raw materials.
본 연구에서는 다공성 니켈재료의 원료분말로 활용될 수 있는 hollw 니켈금속분말 계조를 위한 니켈-흑연복합분말의 흑연코어 기화과정에 관하여 실험을 행하였다. 수증개-수소 혼합가스에 의한 복합분말중 흑연코어의 기화온도는 $800^{\circ}C$~$900^{\circ}C$였으며, 약 1시간의 기화반응에 의해 내부가 텅 빈 hollw니켈금속분말을 얻을 수 있었다. 흑연코어의 평균입도가 21$\mu\textrm{m}$인 82.2tw,% 니켈-17.87tw.5 흑연 복합분말로부터 제조된 hollw니켈금속분말을 100Kg/c$\textrm m^2$의 압력으로 압축, 성형한 성형체의 겉보기 기공도는 45%이었으며, 이성형체를 진공로에서 $1150^{\circ}C$ 의 온도로 1시간 소결하여 30%의 기공도와 소재내에 균질한 기공분포를 갖즌 소결체를 얻음으로써 다공성재료 제조시 hollow분말을 원료로 사용하여 재료 내의 기공에 관한 제반사항을 쉽게 조절할 수 있다는 가능성을 확인하였다.