Abstract
Phase equilibria and reaction paths of the superconducting phases and other compatible phases at $850^{\circ}C$ in the Bi-Sr-Ca-Cu-O system were studied. $Bi_2O_3$ was added to $Sr_2CaCu_2O_x$ by 5% up to 40 mole% Bi in the pseudo-binary $Bi_2O_3-(Sr_2CaCu_2O_x)$ system and the heat treated samples were analysed using XRD. SEM, EDS. and DT A. When Bi contents were greater than 35 mole% Bi, liquid phase was formed which was compatible with $Bi_2Sr_2CaCu_2O_8$ phase. The m.p. of $Bi_2Sr_2CaCu_2O_8$ phase decreased as the content of (Sr+Ca)decreased. $Bi_{2+x}Sr_2CaCu_2O_8$ phase first segregated out of liquid phase around $Bi_2Sr_2CaCu_2O_8$ phase during cooling of liquid phase.
Bi-Sr-Ca-O 초전도성계에서 $Bi_2O_3-(Sr_2CaCu_2O_x$)의 pseude binary계를 선택하여 $Sr_2CaCu_2O_x$에 $Bi_2O_3$를 5%단위로 40 cation mole% Bi까지 첨가하면서 $850^{\circ}C$ 초전도상 및 공존하는 상들의 평형 및 반응 경로들을 XRD, SEM, EDS, DTA를 이용하여 분석하였다. Bi의 함량이 35 mole% Bi보다 클 때에는 $Bi_2Sr_2CaCu_2O_8$상과 공존하는 액상이 형성되며 2212상의 액상으로 존재하며 액상의 냉각시 제일 먼저 $Bi_2Sr_2CaCu_2O_8$상 주의에 석출된 것이 관찰되었다.