Effects of $Ta_2O_5,ZrO_2$ and $SiO_2$ addition on magnetic properties of 0.02wt%$Bi_2O_3$ and 0 . 0 5 wt%$CaCO_3$ doped Mn-Zn ferrites(58.5mol% $Fe_2O_3$, 25.5 mol% ZnO) were investigated. E:lectrlcal resistivity and magnetic properties such as the initial permeability($\mu_i$), loss factor(tan$\delta$), coercive force Hc(m0c) were measured. With lncreasing $Ta_2O_5$ and $ZrO_2$ addition, the following effects were observed: I ) Decreasing of the average grain size; 2) lncreasing of the electrical resistivity and initial permeability; 3) Ilecreasmg of loss factor values. (very low loss esprcially at high frequency region) ; 4 ) Fine and uniform microsrructures were obtamed at O.lwt% nddecl samples. In case of $SiO_2$ addition, anomalous grain growth and degradation of magnetic properties were observed. The obtained maximum initial permeability value was 6260 at IOkHz. $25^{\circ}C$ from 0.02wt%$Bi_2O_3$. 0.05wt%$CaCO_3$, 0.lwt%$Ta_2O_5$ added sample, the corresponded relative loss factor (tan$\delta /\mu_i$)for the sample was $4.2 \times 10^{-6}$.
기본조성 52.5mol% $Fe_2O_3$, 25.5mol% MnO, 22mol% ZnO로 구성된 Mn-Zn페라이트에 $Bi_2O_3$ 및 $CaCO_3$을 각각 0.02, 0.05wt%첨가한 시편에 대해서 $Ta_2O_5,ZrO_2$및 $SiO_2$의 미량 첨가한 따른 미세구조와 자기적 특성변화를 조사하였다. $Ta_2O_5,ZrO_2$첨가에 따라 결정립 크기가 감소되었고, 전기시 균일한 입자로 형성된 미세구조를 가진 재료를 얻었다. $SiO_2$첨가에 따라 결정립의 이상성장이 관찰되었고 소결밀도, 전기저항, 초투자율은 감소하고 고주파 영역에서 상대손실이 증가되었다. 본 연구결과 초투자자율은 균일한 결정립에서 최대의 값을 가지며 0.02wt%$Bi_2O_3$, 0.05wt%$CaCO_3$, 0.1wt%$Ta_2O_5$ 첨가시편의 경우 10kHz, $25^{\circ}C$에서 초투자율($\mu_i$)은 6260이고 상대손실 계수(tan$\delta /\mu_i$)는 $4.2 \times 10^{-6}$ 인 높은 투자율과 낮은 손실 특성을 가진 자성재료를 얻었다.