Abstract
To make the electrophotographic photoreceptor that srnsirizes for panchromatic matcrial, the dying element of sunfasr yellow which has an absorption ivavclength at near 400nm, and $\alpha,\beta$-copper phthalocyaninc dying elements with 700nm absorption wavelength were adsorbed and then dispersed onto the zine oxide(Zn0). In ordcr to characterize rhe change In sensitivity the various binders and different mole ratio of ZnO to binder were employed in here. It was found rhat the optimum sensitivity was obtained with 5.5 ratio. I;rom the measurements of electrostatic and spectral sensitivity, it was found that the maximum photographic properties were obtained for mixing the sunfast yellow and $\beta$-copper phthalocyaninr. In this case the electrophotographic sensiri\ity was found to he $E{1:2}$= 1440 lux . sec. And also the spectral sensitivity shows that it had a good properties for panchromatic matcrial.
본 연구는 가시부 전영역에 감광하는 전자사진용 감광체를 만들기 위하여 400nm부근에 흡수파장을 갖는 sunfast yellow와 700nm부근에 흡수파장을 갖는 $\alpha$,$\beta$-copperphthalocyanine의 색소를 산화아연(ZnO)에 흡착분산시켰다. 각종 결합제(Binder)의 감도와 , 산화아연과 결합제와의 조성비에 따르는 변화실험의 결과 5.5:1에서 가장 좋은 결과를 나타냈다. 전자사진 감광체의 적합성을 확인하기 위하여 정전특성과 분광감도를 측정해 본 결과 sunfast yellow와 $\beta$-copper phthalocyanine을 혼합사용한 것이 가장 좋은 감도를 나타냈으며, 이 때 측정된 전자시진감도는 $E_{1:2}$=1440 luxㆍsec이었다. 또한 분광감도 측정결과는 가시부전역에 걸쳐 감도를 감광체임을 확인하였다.