Abstract
Ni-graphi~e composite powders were prepared by reduct ion of $Ni^{++}$ from arnmoniacal nickel sulfate solution on graphite core by hydrogen gas at elevated temperature and pressure. Effect of coating catalyst. Anthraquinone $(C_6H_4COC_6H_4 CO)$, on the reduction rate and the properties of nickel layer were investigated by SEM, X-ray, size and chemical analysis. 1nduct.ion period, a time lag between the ~njection of hydrogen gas and the start of the reduction, was 22 to 70 mins and was affected by the size and amount of Anthraquinone. Kickel layer deposited on the surface of graphite core material was composed of nickel nodules whose sizes were different with vari~ ous reduction conditions. Minimum diameter of nickel nodules was about 2-3$\mu \textrm m$.
니켈-흑연 복합분말은 고온 고압하에서 수소개스를 사용하여 ammoniacal황산니켈염 수용액으로 부터 니켈이온을 흑연코어표면에 석출시켜 제조하였으며, SEM. X-선 회절분석, 입도 및 화학분석 등을 이용하여 환원속도 및 니켈코팅층의 특성에 미치는 코팅 촉매제 Anthraquinone$(C_6H_4COC_6H_4 CO)$ 의 영향을 조사하였다. 코팅촉매제의 입도 및 첨가량 변호에 따라 수소개스 주입 후 환원반응이 시작되기 까지 필요한 잠복기는 22~70분 정도 이었으며, 흑연코어 표면의 니켈코팅층은 포도송이 모양(botryoidal)인 미립의 니켈 nodule(2-4$\mu\textrm{m}$)로 형성되었다. 또한 코팅촉매제의 첨가량이 증가함에 따라 코팅용액중 니켈이온의 환원속도는 증가하여 0.2gr/$\ell$첨가시 4.5gr/$\ell$/min를 나타내었다.