Abstract
Methacryloxyethyl dimethyl alkyl($C_{1}\sim C_{12}$, benzyl and 2, 2-diethoxy ethyl) ammonium bromide monomers were prepared to investigate the relative humidity characteristics for polymer electrolytes with different chemical structures. They were coated on the alumna substrate printed comblike gold electrode by photopolymerization after micro-syringe injection. As the thickness of rhe humid membrane increased, the impendance decreased, whereas the impedance ~ncreased as the carbon cham of alkyl substituent in the monomer increased. The impendance of the polymeric electrolytes with $C_6\sim C_8$ substituents were varied from 19M$\Omega$ to 5K$\Omega$ for the range of 30-90% Mi. The temperature depedence coefficient in the range of 15-$35^{\circ}C$ was found to be -0.45% $RH/^{\circ}C$and the hysteresis falled within the range of $\pm$2% RH. The response time was 35 second for varying humldity from 33% to 85% RH.
고분자 전해질의 화학구조가 감습특성에 미치는 효과를 조사하기 위하여 $C_{1}\sim C_{12}$의 알킬,benzy1, 2,2-diethoxy dthy1기가 치환된 메타크릴계 4차 암모늄 단량체들을 합성하였다. 이들의 감습용액을 0.15mm간격의 빗살 모양의 금전극이 인쇄된 알루미나 기판에 마이크로 주사기로 도포하여 광중합 후 상대습도에 따른 임피던스 변화를 측정하였다. 도포된 막의 두께가 증가하면 임피던스는 감소하고, 치환기의 탄소 길이가 증가할수록 임피던스는 증가하였다. $C_6\sim C_8$의 알킬기를 가지는 고분자 전해질의 감습특성은 30-90% RH 범위에서 18M$\Omega$-5K$\Omega$의 직선적인 임피던스 변화를 보였다. 또한 임피던스는 온도 의존성을 보여주며 온도가 증가하면 임피던스가 감소하며 온도 의존성 계수는 -0,45% $RH/^{\circ}C$이다. 히스테리시스는 $\pm$2%RH이내이며, 33%-85% RH 사이에서의 응답 속도는 약 35sec이었다.