Abstract
It was investigated to obtain the relationship between magnetic properties and conditions of forming $Fe_{3}C$ single phase from acicular goethite by heat treatment under the atmosphere of CO and $N_{2}$ mixed gas. X-ray analyses, TEM and VSM measurements were imployed for the characteristics of the carbide. Acicular goethite was sinthesized under proper process parameters. $Fe_{3}C$ single phase was obtained above $550^{\circ}C$, 60min. and $Fe_{5}C_2$ was formed with $Fe_{3}C$ below that temperature. The soturation magnetization of $Fe_{3}C$ single phase was about 100emu/g regardless of the reaction temperature. The coersive force and the ratio of Mr/Ms decreased respectively from 780 to 400 Oe. and from 0.35 to 0.13 with increasing reaction temperature.
침상의 괴타이트 합성조건을 구하고 Co/가스에 의한 침탄법으로 $Fe_{3}$C 단상을 얻을 조건을 구하여 그 자기적 특성을 조사한 결과 침상의 괴타이트는 공기 유입량을 1500ml/min, 반응온도 $50^{\circ}C$의 조건하에서 교반속도 500rpm, pH 12.0 이상에서 이상적인 분말을 합성할 수 있었으며 교반속도가 증가할수록 미세하고 입도 분포도 좁고 균일하였다. 탄화반응은 유리탄소를 방지하기 위하여 CO가스와 $N_{2}$가스를 1:2로 혼입하였으며 $550^{\circ}C$, 60min. 이상의 반응조건하에서 $Fe_{3}C$단상의 포화자화값은 탄화반응 온도에 관계없이 100/emu/g으로 일정하였으며 보자력은 780 에서 400Oe까지, 각형비는 0.35에서 0.13까지 탄화잔응 온도가 증가할수록 감소하였다.