Fatigue Crack shape Variations by a Residual Stress and Fatigue Life Predition

잔류응력에 의한 피로균열면 형상변화 및 수명예측

  • 강용구 (금오공과대학교 기계설계공학과) ;
  • 서창민 (경북대학교 기계설계과) ;
  • 박원종 (동환산업㈜기술연구소)
  • Published : 1993.12.01

Abstract

Fatigue crack shape variation by a residual stress during crack growth and life predition are studied. An analytical method is presented to predict the influence of a residual stress due to heattreatment on crack shape variations. Computer simulation results using this me thod are graphically shown that crack growth rate to surface direction are decreased due to compressive residual stress exisiting in surface area. These results are commpared with experimental results. The fatigue life is also predicted by computer simulation of crack aspect ratio variation which is based on the surface crack length increment per unit cycle calculated from a-N diagram. Predited life is about 12 percent lower than experimental life.

Keywords

References

  1. ASTM STP 791 v.1 Stress-Intensity Factor Equations for Cracks in Three-Dimensional Finite Bodies Newman,J.C.Jr;Raju,I.S.
  2. ASTM STP 677 Growth of Part-thorugh Cracks Hodulak,L.;Kordisch,H.;Kunzelmann,S.;Sommer,E.
  3. ASTM STP 687 Aspect Ratio Variability in part-through Crack Life Analysis Engle,R.M.Jr.
  4. ASTM STP 905 Growth behavior of Surface Cracks in the Circumferential Plane of Solid and Hollow Cylinders Forman,R.G.;Shivakumar,V.
  5. ASTM STP 905 Extension of Surface Cracks During Cyclic Loading Muller,H.M.;Muller,S.;Munz,D.;Neumann,J.
  6. ASTM STP 791 v.1 Geometry Variations During Fatigue Growth of Surface Flaws Jolles,M.;Tortoriello,V.
  7. ASTM STP 677 Effect of Residual Stresses on Fatigue Crack Growth in Steel Weldment under Constant and Variable Amplitude Loads Grzegorz Glinka
  8. Engineering Fracture Mechanics v.24 no.3 Residual Stress Effects in Fatigue Crack Growth Woodtli,J.;Muster,W.;Radon,J.C.
  9. Fatigue. engng mater. struct3 v.13 no.1 Fatigue Crack Growth and Closure Behaviour Through a Compressive Residual Stress field Kang,K.J.;Song,J.H.;Earmme,Y.Y.
  10. ASTM STP 381 Stress Analysis of Crack Paris,P.C.;Sih,G.C.M.
  11. Society of Naval Architects of Japan Journal v.109 Kanazawa,T.;Oba,H.;Machida,S.
  12. Trans. ASME. J. Basic Eng. v.85 A Critical Analysis of Crack Propagation Laws Paris,P.C.;Erdogan,F.
  13. ASTM STP 486 The Significance of Fatigue Crack Closure Elber,W.
  14. 慶北大學校 博士學位論文 表面龜裂의 成長特性에 관한 破壞力學的 硏究 강용구
  15. ASTM E837-85 Standard Test Method for Determinng Residual Stress by the Hole-Drilling Strain Gage Method
  16. KSME Journal v.3 no.2 Growth Behavior of short Surface Fatigue Cracks in 2 1/4Cr-1Mo Steel C.M.Suh;Robert O.Ritche;Y.G.Kang
  17. 기전연구사 v.5 鋼의 熱處理 日本鐵鋼協會