Formation of the Shallow $p^+$ -n Junction by As-Preamorphization Method and Characterization

비소 비정질화 방법에 의한 얕은 $p^+$-n 접합의 형성과 특성분석

  • Published : 1993.11.01

Abstract

In the formation of the shallow p$^{+}$-n junction, the preamorphization method by As$^{+}$ ions was applied in order to avoid the boron channeling effect which is occured during the B$^{+}$ implantation especially with low energy. By As$^{+}$ pre-implant with 60KeV energy and 2*10$^{14}$ cm$^{-2}$ dose, the channelinf of B$^{+}$ ions implanted with 10keV/1.5*10$^{14}$ cm$^{-2}$ can be avoded completely. After the RTA of 1050.deg. C and 10sec, the junction depth was 0.14.mu.m, the leakage current was 20nA/cm$^{2}$(at-5V bias) and the sheet resistance was 107.OMEGA./ㅁ. And the preamorphized Si layer was changed into the perfect crystal si after the RTA.r the RTA.