Measurement of the Third Order Nonlinear Optical Susceptibility of the Conducting Polymer Film by Maker Fringe Method

Maker fringe 방법에 의한 전도성 박막의 3차 비선형 광학 감수율의 측정

We have investigated a method to measure the refractive index, coherence length, and the third order nonlinear optical susceptibility ($x^{(3)}$) of the conducting polymer film. ($x^{(3)}$) of polymer film was obtained, by comparing Maker fringe of polymer film with that of fused quartz, and by calculating the correction factor due to the linear refractive index. The linear refractive index of polymer film was determined from the envelopes of the maxima and minima in the transmission spectrum. Poly ((1,4-phenylenevinylene$)_{0.34}$-co-(2-methoxy-1,4-phen ylene vinylene$)_{0.66}$) [PP$V_{0.34}$-PMP$V_{0.66}$] thin film was prepared by spin coating method. From transmission spectrum and Maker fringe data, we found that the refractive index, coherence length, and the third order nonlinear optical susceptibility ($x^{(3)}$) of the [PP$V_{0.34}$-PMP$V_{0.66}$] are 1.786, 17.86 ${\mu}m$ and 5.8${\times}10^{-12}$esu, respectively.

전도성 고분자 박막의 스펙트럼, 가간섭 길이 및 3차 비선형 광학 감수율의 측정방법을 연구했다. 시료박막의 대한 Maker fringe를 용융석영에 대한 것과 비교하고 선형 굴절률에 의한 효과를 보정하여 3차 비선형 광학 감수율값을 계산했다. 선형 굴절률값의 계산을 위하여는 투과율 스펙트럼에서 투과율의 극대(극소) 값의 포락선이 사용되었다. Spin coating 방법을 사용하여 제작된Poly((1,4-phenylenevinylene$)_{0.34}$-co-(2-methoxy-1,4-phen ylene vinylene$)_{0.66}$) [PP$V_{0.34}$-PMP$V_{0.66}$] 박막에 대해서 투과율 스텍트럼과 Maker fringe를 측정한 후, 이들 data로부터 구한 1907 nm 펌프 파장에 대한 굴절률, 가간섭길이 및 3차 비선형 광학 감수율 값은 각각 1.786, 17.86 ${\mu}m$ 및 5.8${\times}10^{12}$esu였다.