Abstract
The characteristics of the type I and type II SHG in LiB305 crystals grown by TSSG method have been investigated using 1064 nm beam from a Q-switched Nd:YAG laser. The measured phase matching angles and angular acceptance bandwidths were $\theta_m=90^{\circ}, \phi_m=11.6^{\circ}$, <$\delta\theta_{int}L_{1/2}=3.3^{\circ}-cm^{1/2}, \theta\phi_{int}L=0.27^{\circ}-cm^{1/2}$ for type I SHG and $\theta_m=20^{\circ}, \phi_m=90^{\circ}$, TEX>$\delta\theta_{int}L_=0.65^{\circ}-cm, \theta\phi_{int}L^{1/2}=3.5^{\circ}-cm^{1/2}$ for type II SHG, respectively. Thp. type I NCPM temperature of 1064 nm beam was found to be $149^{\circ}C$ with the temperature bandwidth $\DeltaTL$of $4.8^{\circ}C-cm$. An energy conversion efficiency of about 1.8% with 2.6 mm thick LBO crystal at an incident power of TEX>$171 MW/\textrm{cm}^2$ was demonstrated. The measured $d_{32} was 0.74\pm0.05 pm/V$..
이 연구에서는 TSSG 법으로 육성한 LiB3O5(LBO) 단결정의 1064nm 광에 대한 type I 및 type II 제 2 조화파 발생(SHG) 특성을 조사하였다. Type I SHG의 위상정합각은 $\theta_m=90^{\circ}, \phi_m=11.6^{\circ}$였고 angular acceptance bandwidth는 각각 $\delta\theta_{int}L_{1/2}=3.3^{\circ}-cm^{1/2}, \theta\phi_{int}L=0.27^{\circ}-cm^{1/2}$로 측정되었다. Type II SHG의 위상정합각은 $\theta_m=20^{\circ}, \phi_m=90^{\circ}$였고 angular acceptance bandwidth는 각각 $\delta\theta_{int}L_=0.65^{\circ}-cm, \theta\phi_{int}L^{1/2}=3.5^{\circ}-cm^{1/2}$로 측정되었다. Type I NCPM SHG 온도는 $149^{\circ}C$였고 temperature bandwidth $\DeltaTL$은 $4.8^{\circ}C-cm$였다. Nd:YAG 레이저의 peak power 가 $171 MW/\textrm{cm}^2$ 일때 두께가 2.6 mm 인 LBO 결정의 SHG 변환효율은 약 1.8%였고, 이차 비선형 계수 $d_{32}는 약 0.74\pm0.05 pm/V$로 측정되었다.