Effect of reaction factors on the characteristics of Ni-coating layer onto graphite

흑연표면의 니켈코팅층 특성에 미치는 반응인자의 영향

  • Dong Jin Kim (Korea Institute of Geology, Mining and Materials (KIGAM), Taejon 305-350, Korea) ;
  • Hun Saeong Chung (Korea Institute of Geology, Mining and Materials (KIGAM), Taejon 305-350, Korea) ;
  • Myung Kyu Jung (Samsung Aerospace, IBU, Changwon 641-120, Korea) ;
  • Ki Byoung Youn (Dept. of Materials Science and Engineering, Incheon University, Incheon 402-749, Korea)
  • Published : 1994.12.01
Download PDF
⟨ Previous Next ⟩

Abstract

Ni-graphite composite powders were prepared by reduction of $Ni^{++}$ from ammoniacal nickel sulfate solution on graphite core by hydrogen gas. Effect of reaction factors on the reduction rate and the properties of nickel layer were investigated by SEM, Optical Microscopy, size and chemical analysis. Induction period, a time lag between the injection of hydrogen gas and the start of the reduction, was 20~110 mins and affected by the reaction temperature and stirring speed. The reduction rate of $Ni^{++}$ was $4.5g/{\ell}/min$ at optimum condition and increased with increasing reaction temperature and stirring speed.

니켈.흑연 복합분말은 수소가스를 사용하여 ammoniacal 황산니켈염 수용액으로 부터 니켈이온을 흑연입자표면에 석출시켜 제조하였으며, SEM, 광학현미경, 입도 및 화학분석등을 이용하여 니켈이오느이 환원속도 및 코팅층의 특서에 미치는 여러 반응인자의 영향을 조사 하엿다. 반응온도 및 교반속도 변화에 따라 수소가스 주입 후 환원반응이 시작되기 까지 필요한 잠복기는 20~110분 정도이었으며 흑연코어 표면의 니켈코팅층은 포도송이 모양(botryoidal)인 니켈 nodule로 형성되었다. 또한 반응 온도 및 교반속도가 높아짐에 따라 코팅용액중 니켈이 온의 환원속도는 증가하였으며 $130^{\circ}C $, 600~800 rpm 조건에서는 $4.5g/{\ell}/min$를 나타내었다.