Abstract
LiTaO3 single crystals were growth without cracking using Pt-Rh crucible and Ir crucible. The starting composition to get the melt of congruent melting composition, which has been dependent upon the experimental procedure, was taken after fixing the total growing process by the result of preliminary experiments. The Rh contamination from the Pt-Rh crucible was to be neglected if the crystal had been grown under inert atmosphere, which resulted in the crystal color being slightly yellow. This color was decolored after 24 hour's annealing at 1200℃ under air atmosphere. The optimum conditions for the crystal growing and the diameter control were so dependent upon the crucible material in spite of using the crucible of the same size. The liquid-solid interface of LiTaO3 crystal of 1" diameter has been flat if the rotation speed was 45rpm.