Preparation and Characterization of Alumina Thin Film by Sol-Gel Method (II); Synthesis of Alumina Sol for Coating and Preparation of Coating Films

졸겔법에 의한 알루미나 박막의 제조 및 특성(II);코팅용 알루미나 졸의 합성 및 박막 제조

  • 이재호 (연세대학교 세라믹공학과) ;
  • 최세영 (연세대학교 세라믹공학과)
  • Published : 1994.08.01
Download PDF
⟨ Previous Next ⟩

Abstract

As the study for preparation of single-layer anti-reflective coating on glass, the conditions of synthesis of sol for coating and of reproducible coating procedure were investigated. In case of water-based sol, coating was impossible because of poor wettability of sol. The Substitution of solvent with ethanol improved the wettability of sol on the glass surface, and optimum amount of ethanol for substitution was 70 vol%. Maximum specific surface area and total pore volume of water-based sol were 268.7$m^2$/g and 0.315 cc/g, but after substitution, those values increased to 404.1 $m^2$/g and 0.376 cc/g, respectively. The upper limit withdrawl speed of coating in order to get clean coated films without aggregations or stains was 7 cm/min. In case of addition of 0.1 mol HNO3 and substitution with 70 vol% ethanol and heat-treatment at 40$0^{\circ}C$ for 1 hour, thin film with thickness of 94 nm was obtained at withdrawl speed of 4 cm/min. The thickness of thin film was independent of drying time.

Keywords

References

  1. ニュ-ガラス 反射防止ガラス S. Sakka
  2. Sol. Ener. Mat. v.5 Sol-Gel Derived AR Coatings for Sili-con C.J. Brinker
  3. J. Non-Crystalline Solids v.42 The Properties of Gra-dient Index Antireflection Layer on the Phase Sepa-rable Glass Y. Asahara;T. Izumitani
  4. Physics of thin films v.2 Antireflection Coatings for Op-tical and Infrared Optical Materials J.T. Cox;G. Hass
  5. 유리 심포지움 no.7 Sputtering 방법에 의한 AR 코팅 유리의 개발 유병석;김의수
  6. Appl. Opt. v.20 Optical Interference Coatings Prepared from Solution R. Phillips
  7. J. Non-Crystalline So-lids v.100 Multilayer SiO₂and TiO₂Coatings on Glasses by the Sol-Gel Process N. Mohallem
  8. J. Non-Cry-stalline Solids v.139 SiO₂-TiO₂Sol-Gel Coatings L. Armelao
  9. J. Non-Crystalline Solids v.121 The Thickness of Sol-Gel Silica Coating Obtained by Dipping M. Guyliemi
  10. J. Non-Crystalline Solids v.86 The Factor Affecting the Thickness of Sol-Gel Derived Silica Coatings Pre-pared by Dipping I. Strawbridge;P.F. James
  11. Appl. Opt. v.19 no.9 Investigation of Porous Oxides as an AR Coating for Glass Surface B.E. Yoldas
  12. Am. Ceram. Soc. Bull. v.54 no.3 A Transparent Porous Alumina B.E. Yoldas
  13. J. Korean Ceram. Soc. v.29 no.12 Development of Ceramic Composite Membranes for Gas Separation:Ⅳ. Permeation Characteristics of r-Alumina Membra-nes S.H. Hyun;B.S. Kang;D.J. Choi
  14. J. Eng. Res. Institute v.25 no.1 Prepara-tion and Characterization of Alumina Thin Films by Sol-Gel Method (I);Synthesis of Alumina Sol for Coa-ting J.H. Lee;T.I. Yoon;J.M. Ahn;S.Y. Choi
  15. Powder surface area and porosity(2nd Ed.) S. Lowell;J.E. Shields
  16. Handbook of Chemistry and physics(68th Ed.)
  17. J. Phys. Chem. v.68 no.9 Structure and Properties of Amorphous Silicoaluminas. I. Struc-ture from X-ray Fluorescence Spectroscopy and Infra-red Spectroscopy A. Leonard;S. Suzuki;C. De Kimpe