Abstract
The effect of die upset and heat treatment on the magnetic properties of mechanically ground $Nd_{16}Fe_{78}B_{6}$ alloys has been studied. Although stripe domain patterns parallel to the compression direction were observed after die upset, it was found that crystallographic c-axes of a specimen were not completely aligned along the compression direction' which resulted in the decrease of Br. The average grain size of a die-upset specimen annealed for 5 hours at $1000^{\circ}C$ was about $20\mu\textrm{m}$, resulting in reduced values of Br and $_{i}H_{c}$. The maximum magnetic properties (Br=7.8 kG and $(_{i}H_{c}=14\;kOe) were obtained from the magnet die-upset at $750^{\circ}C$ using the alloy powder ground for 13 hours.
건식 기계적 분쇄법을 이용하여 $Nd_{16}Fe_{84-x}B_{x}(x\;=\;5,\;6,\;7,\;8)$ 합금에서 다이업셋과 열처리가 자기적 특성에 미치는 영향을 연구하였다. 기계적 분쇄 이후에 다이업셋하면 시편 전체적으로 압축방향과 평행한 stripe형 자구가 많이 나타나지만 자화용이축인 c축으로 완전하게 정렬되지 않고 있어 잔류자속밀도가 낮다. 다이업셋한 시편을 $1000^{\circ}C$, 5시간 열처리하면 결정립이 약 $20\mu\textrm{m}$으로 성장하여 잔류자속밀도와 보자력이 감소한다. 13시간 동안 기계적 분쇄하여 제조한 분말을 다이업셋$(T:750^{\circ}C,\;\dot{\varepsilon}:0.001/sec,\;{\varepsilon}:60%)$한 시편에서 가장 높은 자기적 특성$(_{i}H_{c}=14\;kOe,\;B_{r}=7.8\;kG)$을 얻을 수 있었다.