Abstract
In this study, new preparation method of LiCoO$_{2}$ was applied to develop cathode active material for Li rechargeable cell, and followed by X-ray diffraction analysis, electrochemical properties and initial charge/discharge characteristics as function of current density. HC8A72- and CC9A24-LiCoO$_{2}$ were prepared by heating treatment of the mixture of LiOH H$_{2}$O/CoCO$_{3}$(1:1 mole ratio) and the mixture of Li$_{2}$CO$_{3}$/CoCO$_{3}$(1:2 mole ratio) at 850 and 900.deg. C, respectively. Two prepared LiCoO$_{2}$s were identified as same structure by X-ray diffraction analysis. a and c lattice constant were 2.816.angs. and 14.046.angs., respectively. The electrochemical potential of CFM-LiCoO$_{2}$(Cyprus Foote Mineral Co.'s product), HC8A72-LiCoO$_{2}$ and CC9A24 LiCoO$_{2}$ electrode were approximately between 3.32V and 3.42V vs. Li/Li reference electrode. Stable cycling behavior was obtained during the cyclic voltammetry of LiCoO$_{2}$ electrode. According as scan rate increases, cathodic capacity decreases, but redox coulombic efficiency was about 100% at potential range between 3.6V and 4.2V vs. Li/Li reference electrode. Cathodic capacity of HC8A72-LiCoO$_{2}$ was 32% higher than that of CFM-LiCoO$_{2}$ and that of CC9A24-LiCoO$_{2}$ was 47% lower than that of CFM-LiCoO$_{2}$ at 130th cycle in the condition of lmV/sec scan rate. Constant cur-rent charge/discharge characteristics of LiCoO$_{2}$/Li cell showed increasing Ah efficiency with initial charge/discharge cycle. Specific discharge capacities of CFM and HC8A72-LiCoO$_{2}$ cathode active materials were about 93mAh/g correspondent to 34% of theretical value, 110mAh/g correspondent to 40% of theretical value, respectively. In the view of reversibility, HC8A72-LiCoO$_{2}$ was also more excellent than CFM- and CC9A24-LiCoO$_{2}$.