The Effect of Circulat Hole Size and Distribution on Strength of Braided Composite

브레이드 복합재료의 원공의 크기와 분포가 재료강도에 미치는 영향

  • 이경우 (서울대학교 섬유고분자공학과) ;
  • 강태진 (서울대학교 섬유고분자공학과)
  • Published : 1994.05.01

Abstract

The effect of hole size and hole-to-hole distance in the braided and laminated composite was studied in terms of tensile strength, pin bearing strength, and flexural strength of S2-glass fiber braided polyester. The tensile strength reduction with hole size was well fitted with he Whitney and Nuismer's prediction for the laminated composite. The characteristic distance was measured to be about 1.6mm for braided composite and 1.8mm for laminated one. The effect of distance between the centers of two circu lar holes on tensile strength was negligible when the distance between these two holes was larger than 4 times of the diameter of circular hole for both braided and laminated composite. The side effect was diminished when the center of hole was located 3 times farther than the diamet.er of the hole. The pin bearing strengths was decreased with the size of pin hole for both braided and laminated composite.

S2-유리 섬유/폴리에스터 브레이드 복합재료에서 원공의 크기 및 원공간 거리 변화가 인장성질, 핀하중 인장성질, 굽힘성질에 미치는 영향을 연구하였다. 원공의 크기에 따른 복합재료의 인장강도의 저하는 Whitney와 Nuismer에 의해 제시된 이론값과 대체로 일치함을 보여주었으며 이때의 특성길이($d_o$)는 브레이드 복합재료는 약 1.6mm, 직물 적층 복합재료는 약 1.8mm가 되었다. 브레이드 복합재료의 원공간 거리 변화에 따른 인장강도의 변화는 두 원공 중심 사이의 거리가 원공 지름의 4배 이상이면 원공간 상호작용이 없었다. 원공의 중심과 측면간 거리에 따른 인장강도의 변화는 원공의중심과 측면간 거리가 원공 지름의 3배 이상일 때 상호작용이 없었다. 핀하중 인장실험에서 브레이드 복합재료와 직물 적층 복합재료 모두 핀의 지름이 증가함에 따라 Bearing Stength는 감소하였다.

Keywords

References

  1. Fiber-Reinforced Composites P. K. Mallick
  2. ASTM STP v.593 J. M. Whitney;R. J. Nuismer
  3. J. Composite Materials v.8 J. M. Whitney;R. J. Nuismer
  4. J. Composite Materials v.9 H. J. Konish;J. M. Whitney
  5. Stress Concentration Factors R. E. Peterson