Crystallization of Coprecipitates Prepared from Lead Nitrate and Titanium Tetrachloride

질산납과 사염화티탄으로부터 제조된 공침물의 결정화

  • 최병철 (영남대학교 금속공학과) ;
  • 이문호 (영남대학교 금속공학과)
  • Published : 1994.08.01

Abstract

The crystallization behavior and structural change of amorphous $PbTiO_{3}$ precursors prepared by coprecipitation method were investigated by XRD, Raman spectra, TEM, and RDF. The precursors were prepared at $45^{\circ}C$ and pH of 9 from a mixed solution of lead nitrate and titanium tetrachloride derived using $H_2O_2$ or $NH_4NO_3$ as an ion stabilizer. The activation energy and temperature for crystallization of the coprecipitate prepared using $NH_4NO_3$ as an ion stabilizer were lower than that derived from the solution containing $H_2O_2$ stabilizer. The amorphous coprecipitate transformed to transient phase and then to crystalline $PbTiO_{3}$. Average interatomic distances of amorphous states decreased with increasing heat-treatment temperature.

공침법으로 제조된 비정질 $PbTiO_{3}$전구체의 결정화거동과 구조적 변화를 XRD, 라만스펙트럼, TEM, RDF등으로 조사하였다. 전구체는 이온안정제로 $H_2O_2$혹은 $NH_4NO_3$를 사용하여 제조된 질산납과 사염화티탄의 혼합수용액으로부터 $45^{\circ}C$, pH 9에서 제조되었다. 이온안정제로 $H_2O_2$를 사용한 경우보다 $NH_4NO_3$를 사용하여 제조된 공침물이 더 낮은 온도에서 결정화가 시작되며 결정화의 활성화에너지도 더 작은 값을 가진다. 비정질의 공침물은 transient phase를 거쳐 결정 $PbTiO_{3}$로 변태된다. 비정질 상태의 평균 원자거리는 열처리온도의 증가에 따라 감소한다.

Keywords

References

  1. Ceram. Bull. v.60 no.2 D.W. Johnson, Jr.
  2. Ferroelectrics v.62 S.R. Gurkovich;J.B. Blum
  3. Ferroelectrics Lett. v.44 M. Takashige;T. Nakamura;Y. Aikawa;M.S. Jang
  4. J. Am. Ceram. Soc. v.69 no.10 O. Yamaguchi;A. Arai;T. Komatsu;K. Shimizu
  5. Mat. Res. Soc. Symposia Proceedings R.W. Schwartz;D.A. Payne
  6. J. Am. Ceram. Soc v.74 no.7 M.H. Lee;B.C. Choi
  7. Korean J. Cryst. v.3 no.1 B.C. Choi;M.H. Lee
  8. 日本公用特許公報 村田充弘
  9. J. Am. Ceram. Soc. v.53 no.5 J. Thomson Jr.
  10. Analytical Chem. v.29 no.11 H.E. Kissinger
  11. Ferroelectrics v.52 T. Nakamura;M. Takashige
  12. Mater. Lett. v.3 no.9;10 J.B. Blum
  13. Phys. Rev. B : Condens. Matter v.7 no.7 G. Burns;B.A. Scott
  14. Helv. Phys. Acta v.49 R.A. Frey;E. Silberman
  15. Phys. Rev. B : Condens. Matter v.11 no.3 F. Cerdeira;W.B. Holzapfel;Bauerle
  16. J. Chem. Phys. v.53 no.7 N.E. Tornberg;C.H. Perry
  17. J. Mat. Sci. v.25 G.R. Fox;J.H. Adair;R.E. Newnham
  18. X-ray Diffraction B.E. Warren
  19. Amorphous Metallic Alloys C.N. J. Wagner;F.E. Luborsky(ed.)
  20. Physics of Amorphous Materials(2nd ed.) S.R. Elliott