Mullitization behavior on the reaction-sintering of ${\alpha} - Al_2O_3/SiO_2$composite powder

${\alpha} - Al_2O_3/SiO_2$복합분말의 반응소결에 있어서 물라이트화 거동

  • Lee, Jong-Kook (Dept. of Materials Engineering, Chosun University) ;
  • Kim, Hey-Soo (Dept. of Inorganic Materials Engineering, Seoul National University) ;
  • Kim, Hwan (Dept. of Inorganic Materials Engineering, Seoul National University)
  • 이종국 (조선대학교 재료공학과) ;
  • 김희수 (서울대학교 무기재료공학과) ;
  • 김환 (서울대학교 무기재료공학과)
  • Published : 1995.04.01
Download PDF
⟨ Previous Next ⟩

Abstract

Sintered bodies were prepared from ${\alpha} - Al_2O_3/SiO_2$ composite powders which each alumina particles were surrounded by silica particles and investigated the mullitization behavior on the process of reaction - sintering. Mullitized reaction was started by formation of amorphous aluminosilicate inter - layer and proceeded by diffusion of alumina through this inter-layer. The growth of mullite was happened along the surface of alumina and controlled by the rate of diffusion.

알루미나 입자표면에 실리카 흡착층을 갖는 복합분말로 제조된 시편을 반응소결시켜 물라이트화 과정을 고찰하였다. 물라이트화 반응은 알루미나와 cristobalite의 계면에서 낮은 알루미나 함량을 갖는 비정질 aluminosilicated 상이 중간층을 형성하면서 시작되고 이 층을 통한 알루미나의 확산에 의하여 물라이트가 성장되었다. 물라이트는 알루미나의 입자의 표면을 따라 성장하였으며 확산에 의해 성장속도가 제어되었다