Development of protection coating material on the surface of insulation tiles of space vehicle

우주선용 고온 절연체의 표면 코팅 재료 개발

The recombination of oxygen and nitrogen atoms on the surfaces of two coating m materials of the Space Shuttle Orbiter (SSO), a reaction cured glass (RCG) and a spinel (C742), was investigated. The recombination probability, $\gamma$, i.e., the probability that atoms im p pinging on the surface will recombine, was measured in a diffusion reactor. Value of $\gamma$ for oxy g gen atom on C742 ($3 {\times} 10^{-2}$) was much higher than that on RCG ($4 {\times} 10^{-4}$) at the tempera t ture of SSO re-entry (ca. 1000K). The higher value of $\gamma$ on C742 indicates a higher number d density of active sites than RCG. It suggests the possibility of designing less active surfaces by i inducing the desorption at lower temperature.

우주 항공 기술의 첨단인 Space Shuttle Orbiter(SSO)의 두 coating material 인 Reaction Cured Glass(RCG)와 Spinel(C742)을 제조하여, 표면 위에 부딪히는 원자들의 재결합 가능성 $\gamma$를 확산반응기에서 측정하였다. SSO의 재진입 온도인 약 1000K에서 C742의 산소 원자들의 재결합 가능성 $\gamma$는 $3 {\times} 10^{-2}$으로 RCG에서의 $4 {\times} 10^{-4}$ 보다는 더 큰 값을 갖는다. C742에서 $\gamma$값이 더 높다는 것은 RCG에서 보다 더 많은 활성점을 갖고 있다는 것을 의미한다. 낮은 온도에서 활성점에 있는 원자의 탈착을 유도함으로써 보다 활성이 낮은 표면 코팅 재료를 개발할 수 있다.