Asymmetric poly(vinyl alcohol) (PVA) membranes were prepared by varying the precipitation conditions of the phase inversion technique, and the influences of precipitation conditions on the water uptake of the membrane were investigate. The degree of water uptake of the membrane increased and reached a certain maximum value, as the precipitation time increased. However, it decreded after that. As the precipition temperauure became lower, the degree of water uptake increased more or less. The addition of a nonionic surfactant to the precipitaon solution was effective reducing the precipitation time by lowering the surface tension of the precipitation solution, but ig didn't change the maximum value of its own degree of water uptake. In addition, the relationship between the degree of water uptake and the separation characteristics and mechanical properies of the membrane were investigated. The selectivity factor of the membrane for pervaperation separation decreased, but the permeate flux increased, respectively, with increasing the degree of water uptake. The tensile strength and elongation of the membrane, respectively, increased to a maximum value with increasing the degree of water uptake, and then decreased abtuptly.
상번전법의 침적조건을 변화시켜 poly(vinyl alcohol)(PVA) 분리막을 제조하고 침적조건이 분리막의 물 흡수에 미치는 영향을 조사하였다. 침적시간의 증가에 딸 분리막의 물 흡수도는 증가하다가 감소하는 경향을 보였으며, 침적온도가 낮을수록 분리막의 물 흡수도가 다소 증가하는 경향을 보였다. 침적용액에 비이온 계면활성제를 첨가하는 것은 침적용액의 표면장력을 감소시켜 침적시간 단축에는 효과적이었으나, 분리막의 물 흡수도의 최고치를 변화시키지 못하였다. 또한, 분리막의 물 흡수도와 분리막의 분리 특성 및 기계적 물성과의 관계를 조사하였다. 분리막의 물 흡수도가 증가함에 다라 분리막의 투과증발 분리 특성의 선택도는 감소하고 투과속도는 증가하였다. 분리막의 물 흡수도의 증가에 따라 분리막의 인장강도와 신율은 증가하다가 최고값을 정점으로 하여 급격히 감소하였다.