Abstract
Sol-Gel derived ferroelectric PZT thin films were fabricated on ITO/Glass substrate. Two kinds of rapid thermal annealing methods, R-I (six times of intermediate and final annealing) and R-II (one final annealing after six times of intermediate annealing) were used for preparation of multi-coated PZT thin films. 2500$\AA$-thick PZT thin films were obtained by the R-I and R-II methods and characterized by microstructure and dielectric properties. In case of using R-II, the microstructure was finer than that of R-I and there was no distinguishable difference in dielectric properties of PZT thin films between the R-I and R-II methods. But dielectric properties were enhanced by increasing perovskite phase fraction with increasing annealing temperature. Measured dielectric constant of PZT thin film annealed at 62$0^{\circ}C$ using the R-I method was 256 at 1kHz. Its remanant polarization (Pr) and coercive field (Ec) were 14.4$\mu$C/$\textrm{cm}^2$ and 64kV/cm, respectively.