Abstract
When ceramic membrance was made from metal salt solution in place of metal akoxide solution, crack free and good adhesion to supporter was optimized for sol stability and good adhesion force. A starting sol was prepared from aluminum oxychloride aqueous solutjion in order to inhibit the grain growthof Al2O3 during heat treatment. The crack free dip coating can't be achieved in 1mol/ι zirconium oxychloride solution because of the high viscosity which interferes with the hydration copolymerization between Al3+ ion and Zr4+ ion. Thus Al2O3-ZrO2 sol stability and viscosity for dip coating was effective when 0.01 mol/ι zirconium oxychloride was added. The minimizing of crack and achieving better adhesion to the supporter wa obtained by microwave drying, surfactant addition and ultrasonic dip coating in wet atmosphere. The result seems to minimize the capillary force and improve the adhesive ability to supporter during the process. Where the average pore size of Al2O3-ZrO2 ultrafilter ceramic membrane measured 17 Å by the BET method and observed γ-Al2O3 phase with tetragonal zirconia after firing at 700℃.