Abstract
A study of the dependence of the magnetoresistance in $glass\[Cu_{x\AA}\NiFe_{50\AA}\Cu_{x\AA}\Co_{50\AA}](X;\=\;8,\;10,\;14,\;18,\;22,\;26,\;28,\;38,\;48,\;58\;\AA,\;N\;=\;2,\;3,\;4,\;10,\;20)$ multilayers prepared by dc magnetron sputtering on the interlayer thickness of Cu (X), the number of multylayer(N) and annealing temperature has been performed. Resistance measurement were made by four terminal method, and the magnetic field applied to perpendicular and parallel for the current. The maximum magnetoresistance(MR) ratio(%) was appeared in the vicinity of $10\;\AA$ in Cu layer, and it was oscillated with the thickness of Cu. The MR ratio was increased with the number of layers N, however the ratio for the N = 4 layers decreased rather than the N = 3 layers. The dependence of the ratio on the annealing temperature was increased to $250^{\circ}C$.
보자력이 다른 NiFe와 Co를 자성층으로 하고 Cu를 사잇층으로 하는 $glass\[Cu_{x\AA}\NiFe_{50\AA}\Cu_{x\AA}\Co_{50\AA}](X;\=\;8,\;10,\;14,\;18,\;22,\;26,\;28,\;38,\;48,\;58\;\AA)$ 다층박막을 D.C magnetron sputtering 방법으로 제작하여 사잇층인 Cu 두께, 적층횟수 및 열처리가 자기저항비에 미치는 영향과 자기 곡선의 변화에 대해 연구하였다. 자기저항 측정시 인가 자장은 전류의 방향과 수평, 수직하게 인가하여 측정하였다. Cu 두께가 대략 $10\;\AA$에서 최대 자기저항비를 보이고 있으며, 두께가 증가함에 따라 진동하는 경향은 나타냈다. 적층횟수에 따라서는 적층횟수가 증가함에 따라 증가하였으며, 단지 4층의 경우에는 오히려 3층 보다 감소하였다. 열처리의 경우 온도의 증가에 따라 증가하다가 $250^{\circ}C$ 이상에서는 다시 감소하는 것을 나타났다.