Abstract
In this research, the processing control of NiCuZn Ferrite has been developed. The relationship between initial permeability and bulk density of NiCuZn Ferrite with processing factors was studied. NiCuZn Ferrite, which calcinated at $700^{\circ}C$ for 3 hours, was ball milled for about 60 hours to make a size of $0.5\mu\textrm{m}$ followed by granulation using spray dryer. The physical properties and the magnetic properties of NiCuZn Ferrite were investigated with the processing factor, such as (i) granule size and forming pressure, and (ii) sintering temperature. The green density of NiCuZn Ferrite was largely depended on the forming pressure rather than its granule size. The green density of NiCuZn Ferrite was increased from $2.484\;g/cm^{3}$ to $3.002\;g/cm^{3}$ with increase in forming pressure. The bulk density of NiCuZn Ferrite was increased from $3.470\;g/cm^{3}$ to $4.754\;g/cm^{3}$ linearly with increase in sintering temperature. The relationship between initial permeability and bulk density of NiCuZn Ferrite was expressed with the empirical equation,$\mu_{i}=a+b_{\rho}+c_{\rho}^2$ at forming pressure and sintering temperature.
본 연구에서는 NiCuZn Ferrite 제조공정의 제어를 위하여 제조공정 변수에 따른 NiCuZn Ferrite의 물성 및 자기적특성의 변화를 검토하여, 겉보기밀도(bulk density)와 초기투자율의 관계를 명확하게 하는 것을 목적으로 하였다. $700^{\circ}C$에서 3시간 하소 한 NiCuZn Ferrite를 약 60시간 볼밀링하여 약 $0.5\mu\textrm{m}$ 입자크기로 분쇄한 후 분무 건조하여 과립화하였다. 본 연구에서는 (1)NiCuZn Ferrite 과립의 크기와 성형압력 변화와 (2)일정한 성형조건에서 소성온도의 변화에 따른 성형체 및 소성체의 물성측정, 그리고 자기적 특성을 검토하였다. NiCuZn Ferrite의 green density는 과립의 크기보다는 성형압력에 더 의존하였으며, 과립의 크기가 $150\mu\textrm{m}$ 이하 일 때 성형압력이 증가 함에 따라 green density는 $2.484\;g/cm^{3}$에서 $3.002\;g/cm^{3}$로 크게 증가하 였다. NiCuZn Ferrite의 bulk density는 소성온도에 의하여 거의 직선적으로 $3.470\;g/cm^{3}$에서 $4.754\;g/cm^{3}$로 증가하였다. 성형압력 변화 및 소성온도 변화에 따른 NiCuZn Ferrite 초기투자율과 겉보기밀도 관계를 비교 검토한 결과, NiCuZn Ferrite의 초기투자율($\mu_{i}$)과 겉보기밀도($\rho$)의 관계를 $\mu_{i}=a+b_{\rho}+c_{\rho}^2$와 같이 실험식으로 표현할 수 있었다.