Observation and Analysis of Dislocation Spacing in the Subgrain boundary on IN 617

IN 617의 아결정립계의 전위간격 분석법에 관한 고찰

  • 안성욱 (한국과학기술연구원 특성분석센터) ;
  • 이종민 (고려대학교 재료공학과)
  • Published : 1995.04.01

Abstract

IN 617 was crept under stresses of 107 and 180 MPa with monotonic deformation to strains of $\varepsilon$= 0.03 - 0.30 at 1073K. In order to determine the distances between the subgrain boundaries, the deformed specimens were examined at magnifications of one hundred thousand times by TEM. In cases . where TEM observations were not possible, subgrain angles($\theta$_{s}=sin^{-1}$(b/s))were measured by Kikuchi diffraction lines. The $\theta$_{k}$ converted from s values measured directly by TEM agreed very well with those measured from Kikuchi lines. Therefore, it was found that the $\theta$_{k}$ values could be used in obtaining s, especially in cases where it is impossible to measure s by TEM.

IN 617의 시편으로 1073K의 온도에서 주로 107과 180MPA의 응력에서 $\varepsilon$=0.03-0.30까지 정압크립변형을 하여, 투과전자현미경(TEM)에서 약 십만배의 배율로 아결정립의 전위간 거리 s를 측정하고, TEM에서 측정이 불가능한 경우, 아결정립계가 이루는 각도 ($\theta$_{s}=sin^{-1}$(b/s))를 Kikuchi line을 이용하여 측정하였다. TEM에서 직접 구한 s 값들을 $\theta$_{s}$값으로 환산하여, Kikuchi line으로 측정한 $\theta$_{k}$값을 비교한 결과 거의 같았다.즉, TEM에서 s의 측정이 불가능할 때, $\theta$_{k}$를 측정하여 s값으로 사용하여도 됨을 알 수 있었다.

Keywords

References

  1. Proc. of the 4th Riso Intern. Symp. on Metallurgy and Materials Science W. Blum;P.D. Portella
  2. Acta Metall. v.25 G. Konig;W. Blum
  3. Acta Metall v.30 D. Caillard;J.L. Martin
  4. Acta Metall. v.30 D. Caillard;J.L. Martin
  5. $Einf\"{u}hrung$ in die Elektronenmikroskopie M.V. Heimendahl
  6. Metall. v.2 K. Schwarzkopff
  7. J. of Applied Physics v.35 M.V. Heimendahl;W. Bell;G. Thomas
  8. Phys. Stat. Sol. v.(a)2 P.H. Pumphrey;K.M. Bowkett
  9. Phys. Stat. Sol. v.(a)75 H.O. Martikainen;M.A. Korhonen;V.K. Lindroos
  10. 대한금속학회지 v.30 no.3 안성욱