Abstract
To get optimum synthetic condition of zeolite A made from Kampo natural bentonite, the effects of reactant mole fraction, reaction temperature, and reaction time were studied. The source of silica was 40% -H₂SO₄ treated natural bentonite and that of alumina was synthesized NaA1O₂. The reactant was mixed at the mole ratio of SiO₂ : Al₂O₃ : Na₂O : H₂O=2 : 1 : 1 : 25 and 2 : : 1 : 37. The mixed reactants were aged at 60℃ for 1hr and reacted at 90℃, 100℃ and 120℃ for 1, 3 and 5hr. The optimum synthetic condition was SiO₂ : A1₂O₃ : Na₂O H₂O=2 : 1 : 1 : 30 at 90℃ for 3hr and the synthetic zeolite A prepared by this optimum condition showed the dehydration temperature at 79.2℃ and lattice trans-formation at 503.3℃. The wright loss of water was 5.9%.
경북 감포지역에서 산출되는 천연 벤토나이트를 이용하여 제올라이트 A를 합성하기 위해 반응기질의 몰비, 반응온도, 반응시간 등에 따른 최적의 합성조건을 조사하였다. 실리카원은 40%-황산용액으로 처리한 천연 벤토나이트를 사용하였고, 알루미늄원은 NaA1O₂를 합성하여 사용하였다. 반응기질의 몰비는 SiO₂ : A1₂O₃ : NaO₂ : H₂O=2 : 1 : 1 : 25와 2 : 1 : 1 : 30이었고, 60℃에서 1시간 묵힘과정을 거친 후 90, 100, 120℃에서 1, 3, 5hr반응시켰다 제올라이트 A의 최적의 합성조건은 SiO₂: Al₂O₃ : Na₂O = H₂O=2 : 1 : 1 : 30이고, 90℃에서 3hr 반응시키는 경우였고, 이 조건에서 합성된 제올라이트의 열적 성질은 79.2℃에서 층간수가 증발하였고, 503.0℃에서 결정수가 탈리되었다. 수분의 감소량은 제올라이트 중량비의 5.9%이었다.