Abstract
It was investigated that reinforced species, billet condition and extrusion variation in Al 6061 composite material effected on extrusion process of particulate reinforced composite material. The strength of composite material with reinforcement species revealed SiC$\sub$w/> A1$_2$O$\sub$3f/ > A1$_2$O$\sub$3f/ > A1$_2$O$\sub$3f/ orderly. K$\sub$w/ increased as volute fraction increased in all composite material. The composite materials reinforced by A1$_2$ $O_3$required the larger pressure in hot extrusion process than those by SiC$\sub$p/ at all condition. Extrusion process tended to decrease as the semi-angle of extrusion dies increased because larger contact area caused larger shear friction. Extrusion temperature went up about 50$^{\circ}C$ in low elevated deformation temperature. In extrusion temperature above 500$^{\circ}C$, severe tearing occurred on extrusion surface. More reinforcement in volume fraction, more hot tearing.
분말야금법으로 제조된 A6061기 입자분산강화 복합재의 열간압술가공에 있어서 압출특성에 미치는 강화입자의 종류, 빌렛특성 및 암술조건의 영향에 대하여 조사하였다. A6061기 복합재료의 열간 압술 전단 변형저항에 미치는 강화입자종류의 영향은 Si $C_{w}$ > A1$_2$ $O_{3f}$ > A1$_2$ $O_{3f}$ > Si $C_{p}$의 순으로 되었으며, 모든 강화입자에서 부피분율이 증가함에 따라서 Kw값도 증가하였다. 압출조건, 강화입자의 첨가량 및 첨가입자의 평균입도에 관계없이 A1$_2$ $O_{3p}$가 첨가된 복합재의 열간압출가공에 필요한 소요압력은 Si $C_{p}$의 경우보다 컸다. 압출압력은 압출 다이스 반각이 커질수록 감소하는 경향은 나타났다. 이것은 다이스 반각에 의해 생성되는 빌렛과의 접촉면적이 증가하여 전단마찰응력(m $k_3$)이 상승하기 때문이다. 압출시 압출온도 상승은 저온에서 ~$50^{\circ}C$ 정도 증가하였으며, 압출온도가 50$0^{\circ}C$ 이상이 되면 압출재 표면에 극심한 tearing이 발생하였다. 강화입자의 첨가량이 증가할수록 이 현상은 더 심하게 되었다.게 되었다.