Abstract
Several intermediate glasses are investigated to bond the alumina and the hydroxyapatite (HAp). The chemical compositions of the intermediate glasses are chosen as $CaO-Al_2O_3$. The mole ratio of CaO/$Al_2O_3$ is changed from 0.5 to 3.0. The lowest melting is observed at $1355^{\circ}C$ in the specimen of CaO/$Al_2O_3$ at the mole ratio of 2. With increasing contents of $Al_2O_3$, the melting temperatures gradually increase and a number of pores are observed. The sectional microstructure shows that the good wetability is observed in higher contents of CaO specimens. This implies that the good wetability is obtained in the mole ratio range of CaO/$Al_2O_3geq2$. The phase transformations are observed after treatment but the major peaks of HAp still exist.
알루미나와 Hydroxyapatite(HAp)의 결합을 연구하기 위하여 9 가지의 중간 유리상을 연구하였다. 그 중간상의 화학 조성은 $CaO-Al_2O_3$에서 정하였으며 CaO/$Al_2O_3$의 몰 비율은 0.5에서 3 까지 변화 시켰다. 가장 낮은 용융은 CaO/$Al_2O_3$의 몰 비율이 2이고 $1355^{\circ}C$때 나타났다. $Al_2O_3$의 양을 증가시킴에 따라 용융점은 점점 높아 졌고 많은 기공들이 발견 되었다. 단면 조직 조사에 따르면 높은 CaO양 시편에서 양호한 흡수접착을 발견할 수 있었고, 이것은 CaO/$Al_2O_3$ 비가 2보다 큰것에서 더좋은 흡수접착을 얻을 수 있음을 의미한다. 열처리후 상변태는 발견되었으나, HAp의 중요한 피크는 그대로 남아 있음을 알 수 있다.