초록
This study was performed to compare the anticarious effect of the different fluoride adsorbed(Naf, $NH_4F, Na_2PO_3F, SnF_2, TiF_4$) on synthetic hydroxyapatite and enamel. The amount of fluoride adsorbed in synthetic hydroxyapatite under various concentrations and pH of these fluoride solutions was measured by specific electrode. Enamel samples treated with 5 kinds of 1,000ppm fluoride solutions for 10 minutes were evaluated for fluoride uptake and enamel soubility. The results were as follows. 1. The adsorption of fluoride on synthetic hydroxyapatite increased gradually by the concentration of the fluoride solution, In 1,000ppm fluoride solution, the adsorption of fluoride on synthetic hydroxyapatite treated with NH4F and NaF solutions at pH 4.0 was relatively higher than that of other fluoride solutions. In NH4F and NaF solutions, the adsorption of fluoride on powdered enamel was higher at pH 4.0 solution than at pH 7.0 solution. 2. Fluoride uptake from NH4F solution was relatively high. But that from $Na_2PO_3F$ solution was lower than those from other fluoride solutions. 3. Fluoride solutions were significantly effective on enhancing acid resistance. $NH_4F$ solution was relatively more effective than others on enhancing acid resistance. 4. $SnF_2 and TiF_4$ solutions had the same effect on fluoride adsorption, fluoride uptake, and enamel solubility.