Characteristics of InSb MIS device prepared by remote PECVD SiO$_{2}$

Remote PECVD SiO$_{2}$ 를 이용한 InSb MIS 소자의 특성

InSb MIS devices prepared by remote PECVD SiO$_{2}$ were fabricated. The SiO$_{2}$ films on InSb were deposited at atemperature range of 67~190$^{\circ}$C. The effects of deposition temperature on the structural characteristics of the SiO$_{2}$ films evaluated Auger electron spectroscopy showed that atomic raito of silicon to oxygen was 0.5 and composition toms were distributed uniformaly throuout the oxide film. The transition region is about 100$\AA$ for SiO$_{2}$/InSb interface. The leakage current density at 1MV/cm and the breakdownelectric field of the MiS device using SiO$_{2}$ film deposited at 105$^{\circ}$C were about 22 nA/cm$^{2}$ and 3.5MV/cm, respectively. The interface-state density at mid-bandgap extracted from 1 MHz high frequency C-V measurement was about 2X10$^{11}$ cm$^{-2}$eV$^{-1}$.